When the single screw extruder is in the extrusion molding process, its extruder screw is divided into 3 sections: feeding section (feeding section), melting section (compression section), metering section (homogenization section), these three sections Correspondingly, three functional areas are composed of materials: solid conveying area, material plasticizing area, and melt conveying area. Each area has different temperature requirements, and specific problems should be analyzed in detail. The temperature of the single screw extruder will be briefly introduced below.
What is the general temperature of the solid conveying zone in a single screw extruder?
What is the general temperature in the plasticizing zone of the material in a single screw extruder?
What is the general temperature of the melt conveying zone in a single screw extruder?
What is the general temperature of the solid conveying zone in a single screw extruder?
The temperature of the barrel in the solid conveying zone of the single screw extruder is generally controlled at 100~1400C. If the feeding temperature is too low, the solid conveying zone will be extended, reducing the length of the plasticizing zone and the melt conveying zone, which will cause poor plasticization of the single screw extruder product and affect product quality.
What is the general temperature in the plasticizing zone of the material in a single screw extruder?
The temperature of the material plasticizing zone in the single screw extruder is controlled at 170~1900C. Controlling the vacuum degree of this section is an important process index. If the vacuum degree is low, it will affect the exhaust effect, resulting in bubbles in the pipe, and seriously reducing the mechanical properties of the pipe. In order to make the gas inside the material easily escape, the plasticization degree of the material in this section should be controlled not to be too high, and the exhaust pipe of the single screw extruder should be cleaned frequently to avoid blockage. The vacuum degree of the barrel is generally 0.08~0.09MPa.
What is the general temperature of the melt conveying zone in a single screw extruder?
The temperature of the melt conveying zone in the single screw extruder should be slightly lower, generally 160~1800C. Increasing the screw speed in this section, reducing the head resistance and increasing the pressure in the plasticizing zone are all conducive to the improvement of the conveying rate. For heat-sensitive plastics such as PVC, the residence time should not be too long in this section. The screw speed is generally 20 ~30r/min. The head of the single screw extruder is an important part of extruded product molding. Its function is to generate a higher melt pressure and make the melt shape into a desired shape. The process parameters of each part of the single screw extruder are: die connector temperature 1650C, die temperature 1700C, 1700C, 1650C, 1800C, 1900C.
This is some information related to the use of single screw extruders. The use of single screw extruders is also closely related to the quality of its products. If you need more information, please contact Nanjing JlEYA.
Material delivery method
In a single-screw extruder, there is friction drag in the solids conveying section and viscous drag in the melt conveying section. The friction properties of the solid material and the viscosity of the molten material determine the conveying behavior. If some materials have poor friction properties, if the feeding problem is not solved, it will be difficult to feed the materials into the single-screw extruder. In twin-screw extruders, especially intermeshing twin-screw extruders, the conveying of materials is to some extent forward displacement transmission, and the degree of forward displacement depends on the relationship between the flight of one screw and that of the other screw. the proximity of the relative screw grooves. The screw geometry of the closely intermeshing counter-rotating extruder results in a high degree of positive displacement delivery characteristics.
Material flow velocity field
At present, the flow velocity distribution of the material in the single-screw extruder has been described quite clearly, while the flow velocity distribution of the material in the twin-screw extruder is quite complicated and difficult to describe. Many researchers just do not consider the material flow in the meshing area to analyze the flow velocity field of the material, but these analysis results are very different from the actual situation. Because the mixing characteristics and overall behavior of a twin-screw extruder are primarily determined by the leakage flow that occurs in the intermeshing zone, the flow situation in the intermeshing zone is quite complex. The complex flow spectrum of the material in the twin-screw extruder shows macroscopic advantages that the single-screw extruder cannot match, such as sufficient mixing, good heat transfer, large melting capacity, strong exhaust capacity and good temperature control of the material, etc.
Twin screw extruder is developed based on the single screw extruder, which has been widely used in the molding process of extruded products because of its good feeding performance, mixing and plasticizing performance, exhaust performance, and extrusion stability. So what are the advantages of a twin screw extruder? The following is a detailed introduction.
Here is the content list:
l Wear and tear
l Reduce production costs
l Increase output
l Improve labor efficiency
l High torque and high speed
Wear and tear
Since twin screw extruders are easy to open, the degree of wear of threaded elements and barrel bushings can be detected at any time, so that effective repair or replacement can be carried out. It is not necessary to find out only when there is a problem with the extruded product, which causes unnecessary waste.
Reduce production costs
When producing masterbatches on twin screw extruders, it's usually necessary to alter colors, and if a product amendment is critical, to open the open process space within several minutes, in addition to analyzing the mixing process by looking at the melt profile on the entire screw. The current common twin screw extruder needs to be cleared with a large amount of clearing material when changing colors, which is time consuming, power consuming, and a waste of raw material. The split twin screw extruder can solve this problem. When changing the color, it only takes a few minutes to quickly open the barrel for manual cleaning, so that no or less cleaning material can be used, saving costs.
Increase output
Twin screw snack extruders use side feeding technology to improve the integrity of the material and greatly increase production. The position and shape of the feed opening also have a great influence on feeding efficiency. With the same parameters, the output increases with an increase in the feed area. A rectangular cross section has a higher feed efficiency than a circular cross section for the same inlet area. The use of side by side twin screw feeds is also based on this consideration.
Improve labor efficiency
During equipment maintenance, ordinary twin screw extruders often have to remove the heating and cooling system before the screw can be withdrawn as a whole. In contrast, the split twin screw does not need to be opened by loosening a few bolts and turning the worm gearbox handle device to lift the upper half of the barrel, and then the entire barrel can be repaired. This shortens the maintenance time and reduces the labor intensity.
High torque and high speed
At present, the event trend of twin screw extruders within the world is to develop within the direction of high torsion, high speed, and low energy consumption, and also the impact of high speed is high productivity. The split twin screw extruder belongs to the current class, and its speed will reach and five hundred revolutions per minute. Therefore, its distinctive benefits in process high viscousness and warmth sensitive materials.
In the high speed, high torque core technology, asymmetric and symmetric high torque gearbox currently only Germany and Japan related manufacturers master the core technology, its speed can reach up to 1800 rpm or more, and domestic also master this core technology, such as Nanjing JlEYA extrusion company, is also currently one of the main choices of domestic high end material processing manufacturers, belongs to the domestic independent innovation national encouragement projects.
If you want to buy twin screw extruders, you can consider our cost effective products. We insist on the tenet of "quality first, customer first" and warmly welcome new and old customers to cooperate with us.
The company focuses on twin screw extruders, micro twin screw extruders, plastic extruders, parallel twin screw extruders, and other research and development and manufacturing as the core of the isotropic rotary twin screw mixing and extruding machine, the application range covers the mixing and modification of granulation, polymerization, deswelling, step molding, recycling, and other fields.
PVC compounding extruder is made by mixing PVC resin with stabilizers, lubricants, and other additives through granulation and then extrusion, or by using powder in one extrusion. what are the application areas of PVC? The following are the details.
Here is the content list:
General soft products
PVC film
PVC foam products
PVC coated products
PVC paste resin
PVC transparent sheet
PVC rigid sheet
Other applications of PVC
General soft products can be extruded into cables, wires, and hoses by the extruder: shoe soles, slippers, various plastic sandals, as well as toys and auto parts by the injection molding machine with various molds.
PVC film After mixing and plasticizing PVC with additives, transparent or colored film of specified thickness can be made by using a three-roller or four-roller calendar, and calendered film can be processed by this method. It can also be cut and heat laminated to process raincoats, tablecloths, curtains, packaging bags, inflatable toys, etc. The wide transparent film can be used for greenhouse, plastic shed, and ground film; the film stretched in both directions can be used for shrink packaging due to its characteristics of shrinkage by heat.
Soft PVC can be used as sandals, insoles, foam slippers, and shockproof and cushioning packaging materials. In addition, it can also be extruded into low-foaming hard PVC sheets and profiles by extruder, which is a new type of building material and can be used as a substitute for wood.
Artificial leather with backing is made by coating PVC paste on cloth or paper and then plasticizing it at 100 degrees Celsius or above (or PVC and additives can be calendered into film and then pressed together with backing); while artificial leather without backing is directly calendered by calender into soft sheet with a certain thickness and then pressed with the pattern. It can be used to make leather bags, leather boxes, book covers, sofas, and car cushions, etc. It can also be made into flooring leather, which is used as the flooring material for buildings.
PVC emulsion or micro-suspension resin is dispersed in a liquid plasticizer to make it swell and plasticize into the plasticized sol, and then add stabilizer, filler, coloring agent, etc. After full stirring for de-bubbling, PVC paste is prepared, and then processed into various products such as coat hangers, tool handles, Christmas trees, etc. by casting, impregnating, or laminating processes.
Impact modifier and organotin stabilizer are added to PVC, which is mixed, plasticized, and calendered into transparent sheets. Then it can be made into thin-walled transparent containers by thermoforming and can be used for vacuum blister packaging such as moon cake boxes, etc. It is an excellent packaging material and decoration material.
PVC hard sheet and plate After adding stabilizer, lubricant, and filler to PVC and mixing, it can be extruded into various caliber hard pipes, shaped pipes, corrugated pipes, and other products by using an extruder, and used as a downpipe, drinking water pipe, electric wire casing or staircase handrail, etc.; the calendered sheet can be overlapped and hot-pressed to make various thicknesses of hard sheets, which can be cut into various desired shapes and can be welded into various chemical resistant tanks, ducts and containers by using PVC welding rod with hot air, etc.
PVC can be processed into rigid profiles using an extruder and used for window and door assembly. In some countries, the doors and windows assembled by PVC rigid profile have occupied the market of windows and doors together with wooden windows and doors, aluminum windows, etc.
If you want to buy PVC compounding extruder, you can consult our company, our company's website is https://www.njjyextrusion.com/
The composition of the single screw extruder: mainly consists of servo motor, reduction box, screw cylinder, nozzle head, filter air, heating and cooling system, touch screen, and SPS control. It is the extrusion host to form.
What are the reasons why the main engine of the single screw extruder cannot be started and the solutions?
What are the reasons and solutions for the high inlet flow of the single screw extruder?
What is the design concept of the single screw extruder?
1. Reasons:
(1) The driving program of the single screw extruder is wrong.
(2) There is a problem with the main engine thread and whether the fuse is blown.
(3) The locking device for the single screw extruder and the main engine works.
2. Treatment:
(1) Check the program of the insert extruder and restart in the correct order.
(2) Check the main engine circuit.
(3) Check whether the lubricating oil pump has started and check the status of the locking device concerning the main engine. The oil pump cannot be turned on and the engine cannot be turned on.
(4) The inverter has not discharged the induction current, turn off the main power supply and wait five minutes before starting.
(5) Check if the emergency button of the single screw extruder has been reset.
1. Reasons: (1) The single screw extruder has an insufficient heating time and a large torque. (2) A certain section of the heating does not work.
2. Treatment method: (1) Use the handwheel when driving the single screw extruder. If it is not easy, extend the heating time or check that the heaters of the individual sections work properly.
The main engine makes an abnormal noise:
1. Reasons: (1) Main engine stock damaged. (2) A specific SCR in the SCR DC power supply of the main engine is damaged.
2. Treatment method: (1) Replace the main engine stock of the single screw extruder. (2) Check the thyristor alignment and replace the thyristor component if necessary.
1. High-speed and high-Yield extrusion based on high quality.
2. The design concept of low-temperature plasticization ensures the extrusion of high-quality products.
3. The two-stage overall design of the single screw extruder reinforces the plasticization function to ensure the adjustment of the high-performance extrusion.
4. Special barrier, comprehensive mixing design to ensure the mixing effect of materials.
5. High torque drop, extra-large pressure bearing.
6. Gears and shafts are made of high-strength alloy steel, cooled, and chipped.
7. High hardness, high finish, extremely quiet.
8. PLC-intelligent control can realize the connection between main and auxiliary machines.
9. The easy-to-monitor human-machine interface makes it easy to understand the processing and machine status.
10. The control method (temperature device) can be changed if necessary.
11. The material is 38CrMoAL/A nitric treatment, wear-resistant.
12 Strict temperature control accuracy, combined with air cooling and water cooling.
13. The single screw extruder has a unique inlet design and complete water cooling.
14. An single screw extruder with a grooved surface of the lower shell has an improved feed function that guarantees a high speed and a high yield of extrusion.
The single screw extruder is increasingly used in industrial production.Nanjing JlEYA has committed itself to offering the best-suited single screw extruders at a reasonable price, and all that is necessary to meet the needs of the customer.
The structure of the engineering plastic twin screw extruder barrel is basically similar to that of the single-screw extruder screw barrel. From the appearance structure, the twin-screw extruder barrel is also divided into an integral barrel and a segmented barrel. The engineering plastic twin screw extruder is an upgrade of the single screw extruder, which has also greatly improved the efficiency of use.
What are the reasons why people choose engineering plastic twin screw extruder?
What is the workflow of engineering plastic twin screw extruder?
What are the essential devices in the engineering plastic twin screw extruder?
1. Improve labor efficiency
When the equipment is repaired, engineering plastic twin screw extruder only needs to loosen a few bolts, turn the worm gear box handle device to lift the upper part of the barrel to open the entire barrel, and then perform repairs. This not only shortens the maintenance time, but also reduces the labor intensity.
2. High torque and high speed
The development trend of engineering plastic twin screw extruder in the world is towards high torque, high speed, and low energy consumption. The effect of high speed is high productivity. engineering plastic twin screw extruder belongs to this category, and its speed can reach 500 rpm. Therefore, it has unique advantages in processing high-viscosity, heat-sensitive materials.
3. Wide range of applications
engineering plastic twin screw extruder has a wide range of applications and can be applied to the processing of a variety of materials
4. High output, high quality
engineering plastic twin screw extruder has other advantages of ordinary extruder, and can achieve high output, high quality and high efficiency.
The engineering plastic twin screw extruder used for profile extrusion is usually tightly meshed and rotated in different directions, although a few also use co-rotating twin screw extruders, generally operating at a relatively low screw speed, about 10 r/ min. The high-speed meshing co-rotating engineering plastic twin screw extruder is used for compounding, venting or as a continuous chemical reactor. The maximum screw speed of this type of extruder is 300-600r/min. Non-intermeshing extruder is used for mixing, venting and chemical reaction. Its conveying mechanism is quite different from intermeshing extruder, which is closer to the conveying mechanism of single screw extruder, although there are essential differences between the two.
Among the straightening devices used in engineering plastic twin screw extruder, the most common one is eccentric, and various types of bending of the core are one of the important reasons for the insulation eccentricity. In sheath extrusion, scratches on the sheath surface are often caused by the bending of the cable core. Therefore, the straightening device in various engineering plastic twin screw extruder is indispensable. The main types of straightening devices are: drum type (divided into horizontal and vertical); pulley type (divided into single pulley and pulley block); winch type, which has multiple functions such as dragging, straightening, and tension stabilization; Press wheel type (divided into horizontal type and vertical type), etc.
The engineering plastic twin screw extruders are used more and more widely in daily life, but its quality has a great influence on the experience of use. Nanjing JlEYA has focused on the production and development of engineering plastic twin screw extruders for more than several years, and they have always put the needs of customers as their top priority.
The main system of the plastic extruder is the extrusion system, which includes screw, barrel, hopper, head, and die. The plastic is plasticized into a uniform melt by the extrusion system and is continuously extruded from the head by the screw under the pressure established in the process. The following are details about the plastic extruder extrusion system introduction.
Here is the content list:
Screw
Barrel
Hopper
Head and mold.
The screw is the most important part of the extruder, which is directly related to the application range and productivity of the extruder and is made of high-strength and corrosion-resistant alloy steel.
The barrel is a metal cylinder, generally made of heat-resistant, high-pressure strength, strong wear-resistant, corrosion-resistant alloy steel or composite steel tube lined with alloy steel. The barrel and the screw cooperate to realize the crushing, softening, melting, plasticizing, exhausting, and compacting of the plastic, and to continuously and evenly deliver the rubber to the molding system. Generally, the length of the barrel is 15-30 times its diameter, so that the plastic is fully heated and fully plasticized as a principle.
The bottom of the hopper is equipped with a cut-off device to adjust and cut off the material flow, and the side of the hopper is equipped with a sight hole and a calibrated measuring device.
The head is composed of alloy steel inner sleeve and carbon steel outer sleeve, the head is equipped with a molding mold, the role of the head is to transform the rotational movement of the plastic melt into a parallel linear motion, evenly and smoothly into the mold sleeve, and give the plastic to the necessary molding pressure. The plastic is plasticized and compacted in the barrel and flows through the neck of the head through a certain flow path through the porous filter plate into the forming mold of the head. The mold core and mold sleeve are properly matched to form an annular gap with decreasing cross-section so that the plastic melt forms a continuous dense tubular cladding layer around the core line. To ensure that the plastic flow channel in the head is reasonable and to eliminate the dead angle of the accumulated plastic, there is often a diversion sleeve placed, and to eliminate the pressure fluctuation of plastic extrusion, there is also a pressure equalization ring set. The head is also equipped with a die correction and adjustment device to facilitate the adjustment and correction of the concentricity of the die core and die sleeve.
The extruder head is divided into an angled head (120o angle) and a right angle head according to the angle between the head material flow direction and the screw centerline. The shell of the head is fixed to the body with bolts, the die inside the head has a die core sitting and is fixed to the head inlet port with a nut, the front of the die core seat is equipped with a die core, the die core and the center of the die core seat has a hole for passing the core line, the front of the head is equipped with an even pressure ring for equalizing the pressure, the extrusion package forming part is composed of die sleeve seat and die sleeve, the position of the die sleeve can be adjusted by bolts through the support to adjust the die sleeve to the die core The position of the die sleeve can be adjusted by bolts through support to adjust the relative position of the die sleeve to the die core, which is convenient to adjust the uniformity of the thickness of the extruded layer.
If you want to buy a plastic extruder or want to know more, you can visit our official website. Our website is https://www.njjyextrusion.com/
Twin-screw extruders have barrels with an extension range of 4 and 6D, allowing for precise process design to meet specific customer requirements. All barrels allow for precise temperature control. Cooling is achieved by cooling water injection and high-performance electric heating rods for direct and fast heating. The auxiliary equipment of the twin-screw extruder consists of a straightening device, a preheating device, and a cooling and heating device. The following is a detailed description of the auxiliary equipment.
Here is the content list:
l Straightening device
l Preheating device
l Cooling device
One of the most common types of plastic extrusion rejects is eccentricity, and bending of the wire core in various patterns is one of the most important causes of insulation eccentricity. In sheath extrusion, scratches on the sheath surface are also often caused by the bending of the cable core. Therefore, a variety of extrusion units in the straightening device is essential. The main types of straightening devices are roller type (divided into horizontal and vertical type); pulley type (divided into single pulley and pulley group); stranded pulley type, which plays a variety of roles such as dragging, straightening, and stabilizing tension; pressure pulley type (divided into horizontal and vertical type), etc.
Cable core preheating is necessary for both insulation extrusion and sheath extrusion. For the insulation layer, especially the thin layer of insulation, the existence of pores should not be allowed, the core can be completely removed from the surface of the water, oil, and dirt through high temperature preheating before extrusion. For the sheath extrusion, the main role is to dry the cable core, to prevent the role of moisture (or moisture around the bedding layer) to make the sheath in the possibility of porosity. Preheating can also prevent the plastic from being extruded due to sudden cooling and residual internal pressure. In the process of extruding plastic, preheating can eliminate the cold line into the high-temperature heat, in contact with the plastic at the mouth of the die to form a disparity in temperature, to avoid fluctuations in plastic temperature and lead to fluctuations in extrusion pressure, to stabilize the amount of extrusion and ensure the quality of extrusion. Extrusion unit is used in the electric heating core preheating device, requires sufficient capacity, and ensures rapid temperature rise, so that the core preheating and cable core drying efficiency. The preheating temperature is restricted by the speed of wire release, generally similar to the temperature of the head.
The formed plastic extrusion layer after leaving the head should be immediately cooled and shaped, otherwise, deformation will occur under the action of gravity. The way of cooling usually uses water cooling, and according to the water temperature is different, divided into rapid cooling and slow cooling. Rapid cooling is the direct cooling of cold water, rapid cooling of plastic extrusion layer sizing is beneficial, but for crystalline polymers, due to sudden heat cooling, easy to internal residual stress in the extrusion layer organization, resulting in the use of the process of cracking, general PVC plastic layer using rapid cooling. Slow cooling is to reduce the internal stress of the product, in the cooling water tank placed in sections of different temperatures of water, so that the product gradually cool down and set, PE, PP extrusion on the use of slow cooling, that is, after hot water, warm water, cold water three cooling.
If you are engaged in a twin-screw extruder-related industry, you can consider our cost-effective products.