How to operate PVC compound extruder- Suppliers Factory Manufacturers From China

PVC compounding extruder is divided into RPVC pipe and SPVC pipe, RPVC pipe is easy to cut, welding, bonding, heating can be bent and therefore very easy to install and use. SPVC pipe has excellent chemical stability excellent electrical insulation and good flexibility and colorability this pipe is often used to replace rubber pipe to transport liquid and corrosive media also used as cable casing and wire insulation pipe, etc. So how do choose raw materials and the operation of PVC compounding extruder? The following is a detailed introduction

 

Here is the content list:

• Raw material selection

• Safety operating procedures

 

Raw material selection

PVC compounding extruder in the production of hard pipe resin should be selected from the lower polymerization degree of SG-5 resin polymerization degree of the higher its physical and mechanical properties and heat resistance is better, but the resin liquidity is poor to bring some difficulties in processing, so generally choose viscosity of 1.7 ~ 1.8 × 10-3Pa-s SG-5 resin is appropriate. Hard pipe generally uses lead-based stabilizers whose thermal stability is good commonly used trisodium lead but its lubricity is poor usually and good lubricity of lead, barium soap type and use. Processing hard tube lubricant selection and use are very important to consider both internal lubrication to reduce intermolecular forces to reduce the viscosity of the melt are conducive to molding and to consider external lubrication to prevent the melt and hot metal adhesion to make the product surface shiny. Internal lubrication is generally used metal soap type external lubrication with low melting point wax. Filler mainly with calcium carbonate and barium barite powder calcium carbonate to make the pipe surface performance of good barium can improve the molding of the pipe easy to shape both can reduce costs but the amount of too much will affect the performance of the pipe pressure pipe and corrosion-resistant pipe is best not to add or add less filler.

 

Safety operating procedures

1. Personnel without induction test and operation training cannot operate the extruder independently. 

2. People who have poor eyesight and slow response can not be on duty to operate. 

3. Before starting the machine to do a good job of environmental health around the PVC compounding extruder equipment, equipment around the pile of items not related to production. 

4. Check the safety settings of the extruder before production for damage and test whether it can work effectively. Check whether the connection bolts are loose and whether the safety guards are firm. 

5. Check the lubrication parts, remove the dirt, and refill the lubricant. 

6. PVC compounding extruder barrel and die heating constant temperature time to ensure that the material temperature does not reach the process requirements when driving production. 

7. Before starting the screw drive motor to use the hand plate support V pulley, should be flexible rotation, no blocking phenomenon; then start the lubricating oil pump work 3min before starting the screw rotation at low speed. 

8. Screw airlift time should not exceed 2 ~ 3min. 

9. PVC compounding extruder barrel before adding material to check the barrel, hopper, there is no foreign matter; raw materials should be free of metal, sand, and other impurities to Prevent damage to the screw. 

10. The screw starts, the transmission parts work sound normal, the main motor current within the allowable rated value, before allowing the barrel to add material, adding material should first be a small amount of evenly added material. 

11. When adjusting the die gap or clearing the dirty material, the operator should wear gloves and not face the barrel and die to prevent the molten material from spraying out of the die and scalding the body. 

12. Extruder driving operation is not allowed to repair, and no one is allowed to do any work on the equipment at this time. 

13. In case of the following phenomena, should be an emergency stop. 

Bearing parts of the high temperature, lubricating oil (grease) out; motor odor, smoke, or shell temperature is too high; speed box lubricating oil temperature, smoke; transmission parts emit irregular abnormal sound; machine work produces violent vibration; screw suddenly stop rotating.

14. PVC compounding extruder equipment on the safety cover and the location of the safety alarm device is not allowed to change at will, not to mention artificially caused by the malfunction. 

15. Find that the equipment leakage, oil leakage phenomenon should be timely maintenance troubleshooting, no water, oil flow around the machine.

 

If you have questions about how to use the PVC composite extruder, you can contact us on the official website. We are happy to answer for you.

 

The main machine of the plastic extruder is the extruder, which is composed of an extrusion system, transmission system, and heating and cooling system. The following is a detailed description of the composition of the plastic extruder.

 

Here is the content list:

• Extrusion system

• Drive System

• Heating and cooling device

 

Extrusion system

A homogeneous melt is plasticized bypassing the plastic through the extrusion system, which consists of a screw, barrel, hopper, head, and die.

 

Drive System

The function of the drive system is to drive the screw, supplying the torque and speed required by the screw during the extrusion process, usually consisting of an electric motor, reducer, and bearings.

The manufacturing cost of the reducer is roughly proportional to its size and weight, provided that the structure is the same. Because the shape and weight of the reducer are large, it means that more materials are consumed in the manufacturing, and the bearings used are also larger, which increases the manufacturing cost.

For a similar screw diameter extruder, the high speed and high potency extruder consume additional energy than the traditional extruder, the motor power is doubled, and also the reducer seat range is raised consequently is critical，however a high screw speed means that an occasional reduction magnitude relation. For the same size reducer, the gear modulus of the low reduction ratio increases compared to the large reduction ratio, and the capacity of the reducer to bear the load also increases. Therefore, the rise in volume and weight of the reducer isn't linearly proportional to the rise in motor power. If the extrusion volume is employed because of the divisor and dividend by the burden of the reducer, the high speed and high potency extruder can have a smaller range and the normal extruder will have a larger number.

In terms of unit output, the small motor power and the small weight of the reducer of the high speed and high-efficiency extruder means that the manufacturing cost per unit output of the high speed and high-efficiency extruder is lower than that of the normal extruder.

 

Heating and cooling device

Heating and cooling are necessary to enable the plastic extrusion process to proceed.

(1) Extruders usually use electric heating, which is divided into resistance heating and induction heating, with heating sheets installed in each part of the body, neck, and head. The heating device heats the plastic inside the barrel from the outside to warm it up to the temperature required for the process operation.

(2) The cooling device is installed to ensure that the plastic is in the temperature range required for the process. Specifically, it is to exclude the excess heat generated by the shear friction of the rotating screw to avoid the plastic from decomposing, scorching, or shaping difficulties due to the high temperature. Barrel cooling is divided into two kinds of water-cooled and air-cooled, generally small and medium-sized extrusion machine using air-cooled is more appropriate, large is more water-cooled or a combination of two forms of cooling; screw cooling is mainly used in the center of water-cooled, the purpose is to increase the rate of solid material delivery, stabilize the amount of rubber, while improving product quality; but the cooling at the hopper, one is to strengthen the role of solid material delivery, to prevent the plastic grain sticky blockage because of the heating the second is to ensure the normal work of the transmission part.

 

If you are engaged in the industry related to the extruder, you can consider our cost-effective products. Our company is a leading extruder manufacturer specializing in a twin-screw extruder, micro twin-screw extruder, plastic extruder, and parallel twin-screw extruder in China.

The plastic extruder is a common plastic machinery equipment, in the process of the daily operation of the extruder, the extruder will have a variety of failures, affecting the normal production of plastic machinery, the following we will analyze the extruder failure.

 

Here is the content list:

• Unstable host current

• The main motor can not start

• The head is not discharged smoothly or blocked

• The main electric starting current is too high

• The main motor makes an abnormal sound

 

Unstable host current

1. Production reasons.

(1) Uneven feeding.

(2) The main motor bearing of the plastic extruder is damaged or poorly lubricated.

(3) A section of the heater is out of order and does not heat up.

(4) The screw adjustment pad is not correct, or the phase is not correct, and the component interferes.

2. Treatment methods.

(1) Check the feeder, troubleshooting.

(2) Overhaul the main motor of the plastic extruder, replace the bearings if necessary.

(3) Check whether each heater is working properly, replace the heater if necessary.

(4) Check the adjustment pad, pull out the screw to check whether there is interference with the screw.

 

The main motor can not start

1. Causes.

(1) There is a mistake in the start-up procedure of the plastic extruder.

(2) The main motor thread has a problem, whether the fuse is burned ring.

(3) The main motor-related chain device to function

2. Treatment methods.

(1) Check the program, reboot the machine in the correct boot sequence.

(2) Check the main motor circuit.

(3) Check whether the lube oil pump of the plastic extruder is started and check the status of the chain device associated with the main motor. The oil pump is not on and the motor cannot be turned on.

(4) The inverter induction power has not been discharged. Turn off the main power and wait for 5 minutes before starting again.

(5) Check whether the emergency button is reset.

 

The head is not discharged smoothly or blocked

1. Causes.

(1) A section of the heater does not work, and the material is not plasticized well.

(2) The operating temperature setting is low, or the molecular weight distribution of plastic is wide and unstable.

(3) There may be foreign substances that do not melt easily.

2. Treatment methods.

(1) Check the heater of the plastic extruder and replace it if necessary.

(2) Verify the set temperature of each section, and if necessary, consult with the technician to increase the temperature setting.

(3) Clean and check the extrusion system and the head.

 

The main electric starting current is too high

1. Causes.

(1) Insufficient heating time and high torque.

(2) A section of the heater does not work.

2. Treatment methods.

(1) Apply hand pan machine when starting, if not easy, extend the heating time or check whether each section heater is working properly.

 

The main motor makes an abnormal sound

1. Produced by.

(1) The main motor bearing of the plastic extruder is damaged.

(2) The main motor silicon controlled rectifier line in silicon controlled damage.

2. Treatment methods.

(1) Replace the main motor bearings.

(2) Check the silicon-controlled rectifier circuit, if necessary, replace the silicon-controlled components.

 

Our company's website is https://www.njjyextrusion.com/. If you still have questions, you can contact us on the official website.

Today, we loaded 2x40HQ export to Vietnam.

One is SHJ-50 twin screw extruder, the other is SHJ-72 twin screw extruders. Both extruders are used for making filler masterbatch.

Nanjing Jieya is a leading manufacturer of twin screw compounding extruders with over 20 years experience. We will offer you the top quality with best price.

We warmly welcome your inquiry.

The structure of the engineering plastic twin screw extruder barrel is basically similar to that of the single-screw extruder screw barrel. From the appearance structure, the twin-screw extruder barrel is also divided into an integral barrel and a segmented barrel. The engineering plastic twin screw extruder is an upgrade of the single screw extruder, which has also greatly improved the efficiency of use.

• What are the reasons why people choose engineering plastic twin screw extruder?

• What is the workflow of engineering plastic twin screw extruder?

• What are the essential devices in the engineering plastic twin screw extruder?

What are the reasons why people choose engineering plastic twin screw extruder?

1. Improve labor efficiency

When the equipment is repaired, engineering plastic twin screw extruder only needs to loosen a few bolts, turn the worm gear box handle device to lift the upper part of the barrel to open the entire barrel, and then perform repairs. This not only shortens the maintenance time, but also reduces the labor intensity.

2. High torque and high speed

The development trend of engineering plastic twin screw extruder in the world is towards high torque, high speed, and low energy consumption. The effect of high speed is high productivity. engineering plastic twin screw extruder belongs to this category, and its speed can reach 500 rpm. Therefore, it has unique advantages in processing high-viscosity, heat-sensitive materials.

3. Wide range of applications

engineering plastic twin screw extruder has a wide range of applications and can be applied to the processing of a variety of materials

4. High output, high quality

engineering plastic twin screw extruder has other advantages of ordinary extruder, and can achieve high output, high quality and high efficiency.

What is the workflow of engineering plastic twin screw extruder?

The engineering plastic twin screw extruder used for profile extrusion is usually tightly meshed and rotated in different directions, although a few also use co-rotating twin screw extruders, generally operating at a relatively low screw speed, about 10 r/ min. The high-speed meshing co-rotating engineering plastic twin screw extruder is used for compounding, venting or as a continuous chemical reactor. The maximum screw speed of this type of extruder is 300-600r/min. Non-intermeshing extruder is used for mixing, venting and chemical reaction. Its conveying mechanism is quite different from intermeshing extruder, which is closer to the conveying mechanism of single screw extruder, although there are essential differences between the two.

What are the essential devices in the engineering plastic twin screw extruder?

Among the straightening devices used in engineering plastic twin screw extruder, the most common one is eccentric, and various types of bending of the core are one of the important reasons for the insulation eccentricity. In sheath extrusion, scratches on the sheath surface are often caused by the bending of the cable core. Therefore, the straightening device in various engineering plastic twin screw extruder is indispensable. The main types of straightening devices are: drum type (divided into horizontal and vertical); pulley type (divided into single pulley and pulley block); winch type, which has multiple functions such as dragging, straightening, and tension stabilization; Press wheel type (divided into horizontal type and vertical type), etc.

The engineering plastic twin screw extruders are used more and more widely in daily life, but its quality has a great influence on the experience of use. Nanjing JlEYA has focused on the production and development of engineering plastic twin screw extruders for more than several years, and they have always put the needs of customers as their top priority.

The underwater pelletizing machine is a smart machine with a touch screen, supports touch input, and is equipped with an Android system. The main engine of the underwater pelletizing machine is an extruder, which consists of an extrusion system, a transmission system and a heating and cooling system.

• What are the possible failures of the underwater pelletizing machine and their solutions?

• What are the advantages of the underwater pelletizing machine?

• What are the applicable materials for the underwater pelletizing machine?

What are the possible failures of the underwater pelletizing machine and their solutions?

Cause analysis: underwater pelletizing machine cutter wears excessively or the cutter blade is damaged, the particle water flow is too low, the pelletizer vibration is too large, the cutter and the template are not tightly attached, the material melt index fluctuates, and the discharge flow rate is inconsistent. Excessive water temperature and other reasons can cause the shutdown of the underwater pelletizing system and cause the interlocking shutdown of the entire unit.

Solution: After stopping the underwater pelletizing machine, visually check whether the cutting edge of the cutting knife is excessively worn or damaged. If so, replace the cutting knife completely. Check and confirm whether the granular water leaks internally, whether the filter and cooler of the granular water tank are blocked. If they are blocked, they should be cleaned manually; check whether the inlet and outlet pressures of the granular water pump are normal. If not, check the valves on the granular water pump and the pump pipeline. Check whether the alignment between the cutter shaft and the underwater pelletizing machine is out of tolerance, whether the bearing assembly of the cutter shaft is damaged, and whether the cutter rotor is out of balance. During operation, check whether there is any gap in the contact between the four moving wheels of the pelletizing trolley and the guide rail. Control the volatile matter in the polypropylene powder and eliminate the vibration of the cutter and cutter shaft when it flows through the template hole. Reduce the temperature of the hot oil at the template of the underwater pelletizing machine, check the temperature distribution of the cylinder and the template, and whether the flow, pressure and temperature of the cooling water of the cylinder are normal; confirm the time setting for the "water, knife, material" to reach the template to prevent particles The water reaches the template prematurely and freezes the template hole. After closing the head of the underwater pelletizing machine, the feed volume should be quickly increased to the set load of the extruder.

What are the advantages of the underwater pelletizing machine?

The underwater pelletizing machine is a new model for pelletizing plastic materials that are elastic, easy to foam at low temperature, difficult to form, and have poor flow properties. The underwater pelletizing machine breaks through the traditional method of stranding pelletizing in the past. It overcomes the shortcomings of instability, uneven particles, easy agglomeration, and low output during the granulation of elastomer raw materials.

What are the applicable materials for the underwater pelletizing machine?

The underwater pelletizing machine is suitable for EVA, TPU and other materials with high viscosity and high viscosity of elastomers, and also suitable for conventional materials such as PP, PE, ABS, PA, and PC.

The widespread use of underwater pelletizing machines has continuously increased the demand for them in the market. Nanjing JlEYA, as a Chinese pioneer in underwater pelletizing machine, can ensure the machines’ quality and after-sales service.

When the single screw extruder is in the extrusion molding process, its extruder screw is divided into 3 sections: feeding section (feeding section), melting section (compression section), metering section (homogenization section), these three sections Correspondingly, three functional areas are composed of materials: solid conveying area, material plasticizing area, and melt conveying area. Each area has different temperature requirements, and specific problems should be analyzed in detail. The temperature of the single screw extruder will be briefly introduced below.

• What is the general temperature of the solid conveying zone in a single screw extruder?

• What is the general temperature in the plasticizing zone of the material in a single screw extruder?

• What is the general temperature of the melt conveying zone in a single screw extruder?

What is the general temperature of the solid conveying zone in a single screw extruder?

The temperature of the barrel in the solid conveying zone of the single screw extruder is generally controlled at 100~1400C. If the feeding temperature is too low, the solid conveying zone will be extended, reducing the length of the plasticizing zone and the melt conveying zone, which will cause poor plasticization of the single screw extruder product and affect product quality.

What is the general temperature in the plasticizing zone of the material in a single screw extruder?

The temperature of the material plasticizing zone in the single screw extruder is controlled at 170~1900C. Controlling the vacuum degree of this section is an important process index. If the vacuum degree is low, it will affect the exhaust effect, resulting in bubbles in the pipe, and seriously reducing the mechanical properties of the pipe. In order to make the gas inside the material easily escape, the plasticization degree of the material in this section should be controlled not to be too high, and the exhaust pipe of the single screw extruder should be cleaned frequently to avoid blockage. The vacuum degree of the barrel is generally 0.08~0.09MPa.

What is the general temperature of the melt conveying zone in a single screw extruder?

The temperature of the melt conveying zone in the single screw extruder should be slightly lower, generally 160~1800C. Increasing the screw speed in this section, reducing the head resistance and increasing the pressure in the plasticizing zone are all conducive to the improvement of the conveying rate. For heat-sensitive plastics such as PVC, the residence time should not be too long in this section. The screw speed is generally 20 ~30r/min. The head of the single screw extruder is an important part of extruded product molding. Its function is to generate a higher melt pressure and make the melt shape into a desired shape. The process parameters of each part of the single screw extruder are: die connector temperature 1650C, die temperature 1700C, 1700C, 1650C, 1800C, 1900C.

This is some information related to the use of single screw extruders. The use of single screw extruders is also closely related to the quality of its products. If you need more information, please contact Nanjing JlEYA.

Malfunctions that are caused by inadequate or improper maintenance can result in high repair costs and unnecessarily long gearbox down times. Regular servicing and inspection work are therefore imperative!
All servicing and repair work is only allowed to be performed with the gearbox stationary and by trained,authorized and appropriately instructed personnel.
Refilling lubrication oil
The oil level is to be checked regularly.It must never be below the bottom mark. In the case that the oil level drops below the minimum,it is imperative that the lubricant is topped up. The oil is only allowed to be topped up with the drive units shut down. A funnel with a filter is to be used for toppcng up (filter mesh 40um). The gearbox is always to be filled with the same type of oil as used previously It is not allowed to mix different oils or oils from different manufacturers.
Changing oil
The effectiveness of the oil reduces with increasing use due to soiling (foreign bodies and water)  and  chemical  changes(ageing  products).  When  the  soiling  and/or  ageing  is/are excessive, it is necessary to change the oil. Regular oil analyses provide information on the effectiveness of the gearbox oils. For larger quantities of oil it is recommended to make oil changes dependent on the results of an oil analysis.A missed oil change increases the risk of damage and can result in premature failure of the gearbox.
The first oil change should be made at approx.2500 perating hours.Subsequent oil changes depend on the state of the oil and are to be performed every 4,000 to 6,000 operating hours, however at the latest after one year.
The gear box is the core part of the twin screw extruders, we shall pay attention to its maintenance for long servicelife.

 A plastic extruder performs all of the following processes through a barrel with a screw and auger channel. The plastic pellets enter the barrel through a hopper at one finish of the barrel and are then transferred through the screw to the opposite finish of the barrel. What are the working principle and molding principles of a plastic extruder? The following is a detailed description.

 

Here is the content list:

• Working principle

• Forming principle

 

Working Principle

Pressure and shearing, etc., convert the solid plastic into a uniform and consistent melt and send the melt to the next process. The production of the melt involves processes such as mixing additives such as masterbatches, blending resins, and re-crushing. The finished melt must be homogeneous in consistency and temperature. The pressurization must be high enough to extrude the viscous polymer.

 

To have sufficient pressure, the depth of the threads on the screw decreases as the distance to the hopper increases. The external heating and the internal heat generated in the plastic and the screw due to friction softens and melts the plastic. The design requirements for plastic extruders often vary from polymer to polymer and from application to application. Many options involve discharge ports, multiple loading ports, special mixing devices along the screw, cooling and heating of the melt with or without an external heat source (adiabatic plastic extruders), the relative size of the gap variation between the screw and the barrel, and the number of screws. For example, twin-screw plastic extruders allow for more thorough mixing of the melt than single-screw plastic extruders. Tandem extrusion uses the melt-extruded from the first plastic extruder as feedstock for the second plastic extruder, which is typically used to produce extruded polyethylene foam.

 

D L the characteristic dimensions of plastic extruders are the diameter of the screw (D) and the ratio of the length of the screw (L) to the diameter D L/D (D) (L/D. Plastic extruders usually consist of at least three segments. The first section, near the L/D) filling hopper, is the filling section. Its function is to allow the material to enter the plastic extruder at a relatively smooth rate. In general, this section will be kept at a relatively low temperature to avoid clogging the charging channels. The second section is the compression section, where the melt is formed and the pressure is increased. The transition from the charging section to the compression section can be abrupt or gradual (gentle). The last half, the metering section, is adjacent to the plastic extruder outlet and its main operate is that the uniformity of the fabric flowing out of the plastic extruder. In this section, the material should have sufficient residence time to ensure uniformity of composition and temperature.

 

At the end of the barrel, the plastic melt leaves the plastic extruder through a head that is designed in an ideal shape for the extruded melt stream to pass through.

 

Another important part is the drive mechanism of the plastic extruder. It controls the rotational speed of the screw, which determines the output of the plastic extruder. The power required is determined by the viscosity (flow resistance) of the polymer. The viscosity of the polymer depends on the temperature and flow rate and decreases with increasing temperature and shear. Plastic extruders are equipped with screens that keep impurities out of the screen. To avoid downtime, the screens should be able to be changed automatically. This is especially important when processing resin with impurities, such as recycled material. The extruder's screw is divided into feeding section, plasticizing, melting section, temperature according to the process parameters of the plastic particles, the model according to the diameter of the screw 20, 36, 52, 65, 75, 95, 120, 135. Plastic particles heated by the movement of the screw to change the original state, there are many types, depending on the specific application. The capacity of the frequency conversion is proportional to the diameter of the screw and then adjusted according to the different raw materials.

 

Forming principle

The extrusion method of plastic extruders generally refers to the melting of plastic at a high temperature of about 200°C. The melted plastic is then passed through a die to form the desired shape. Extrusion molding requires a deep understanding of the characteristics of plastics and extensive experience in mold design and is a technically demanding molding method.

Extrusion molding is a method of a continuous flow of material through a die by heating and pressurizing in an extruder, also known as "extrusion molding". Compared with other molding methods, it has the advantages of high efficiency and low unit cost.

Extrusion is mainly used for molding thermoplastics, but it can also be used for some thermosets. Extruded products are continuous profiles, such as tubes, rods, wires, sheets, films, wire, and cable cladding, etc. In addition, it can also be used for mixing, plasticizing and granulating, coloring, blending, etc. plastics.

 

The extruded products can be called "profiles", which are also called "profiles" because of their irregular cross-sectional shape.

Twin Screw Compounding Dawn Denby 2022-08-03T17:18:12-04:00. We Offer Polymer Compounding Using Twin Screw Extruders. ... Our technicians use their knowledge of the compounding process to modify the machine in order to optimally meet the requirements of our customers. Our equipment has excellent mixing and product handling capabilities ...

Eva Twin Screw Extruder (185065 products available) 1/6 TSH-20 Lab/Ekstruder Plastik Sekrup Kembar Mini untuk Pelletisasi US

Detailed Product Description Screw Design: Twi-single Screw Extruder Application: LDPE 85-90%MDH Internal Mixer: 110L Color: Any Color Screw Diameter: 71mm/180mm Motor: 132/55kw Capacity: -500kg Per Hour Cutting Way: Two Stage Air Cooling Die Face LDPE MDH ZL75-180 Two Stage Pellet...

We are Exporter and Manufacturer of Plastic Granules Making Machine, Compounding Machine, Twin Screw Plastic Compounding Machine, Etc. NANJING HUNDRED HORSE PLASTIC MACHINE CO. LTD. - Based in Nanjing, Jiangsu, China. 0

ZHOUSHAN QUNYING SCREW is a China Bimetallic/Nitrided Conical Twin Screw Barrel For Extruder Suppliers and factory.Product detail:Place of Origin: Zhejiang, China (Mainland)Brand Name: QunyingModel Number: …

Co-Rotating Twin Screw Extruder, Granulating Extruder manufacturer / supplier in China, offering SRL-Z300/600L 500/1000L 800/2000L ABB Frequency Inverter PVC WPC Plastic Powder Hot and Cold Mixer Unit Raw Material Mixing Machine, High Quality Two Stage Extruder for High Filler Masterbatch and Polymer PVC Compound, High Speed …

Wholesale Twin Screw Extruder ☆ Find 275 twin screw extruder products from 81 manufacturers

Plastic Sheet Extruder Conic Double Screw Extruder Machine 65/132. a150-300 kg of calcium powder can be added according to the characteristics and requirements of the product. If there are special requirements, a good method can be tested and explored.