Introduction to Twin-screw extruder- Factory Suppliers Manufacturers From China

Plastic extruders can be divided into single-screw extruders, twin-screw extruders, and multi-screw extruders according to their number of screws. The following are the details of the types of plastic extruders.

 

Here is the content list:

• Classification of plastic extruders

• Single-screw extruder

• Twin-screw extruder

 

Classification of plastic extruders

1, According to the number of screws, divided into single-screw extruders, twin-screw extruders, and multi-screw extruders.

2, According to the presence or absence of a screw in the extruder, divided into screw extruders and plunger extruders.

3, According to the running speed of the screw to divide:

Ordinary extruder: speed below 100r/min.

High-speed extruder: speed of 100 to 300r/min.

Super high-speed extruder: the speed is 300~l500r/min.

4, According to the extruder assembly structure classification: there are integral extruders and separate extruders.

5, According to the spatial position of the screw in the extruder, can be divided into the horizontal extruder and vertical extruder.

6, According to whether the extruder is in the process of exhaust and can be divided into exhaust type extruder and non-exhaust type extruder

 

Single-screw extruder

The single-screw extruder occupies an important position both as a plasticizing and pelletizing machine and as a molding machine, and in recent years, the single-screw extruder has developed greatly. Single-screw extruders were the first extruders to gain widespread application in the plastic processing and molding field due to their simple structure and high processing efficiency. Similarly, to meet different processing needs, various equipment manufacturers have explored various screw and barrel structures. The single-screw extruder has evolved from the basic pure screw structure to various structures such as damping screw block, exhaust extrusion, slotted screw barrel, pinned barrel, building block structure, etc., thus enabling the single-screw extruder to have a wider range of molding.

 

Due to the small footprint of single-screw extruders, they are almost the only equipment used in the compounding and blown film fields. Single-screw extruder technology has become an important part of the extrusion process market that cannot be ignored.

 

 

Twin-screw extruder

The twin-screw extruder has less heat generated by friction, more uniform shearing of the material, larger conveying capacity of the screw, more stable extrusion volume, long stay of the material in the barrel, and uniform mixing.

 

The twin-screw extruder has good feeding characteristics, is suitable for powder processing, and has better mixing, exhaust, reaction, and self-cleaning functions than the single-screw extruder, characterized by the processing of plastics with poor thermal stability and co-mingled materials show its superiority. Based on the twin-screw extruder, the multi-screw extruder was developed for easier processing of co-blends with poor thermal stability.

 

If you want to buy an extruder, you can consider our cost-effective products. Nanjing JlEYA is the leading manufacturer extruder manufacturer specializing in a twin-screw extruder, mini twin screw extruder, plastic extruder, and parallel twin-screw extruder in China, which is widely used in compounding, modification, polymerization, after 17 years of development, now we have 20,000 square meters workshop with annual sales over 300+ sets, export over 60 countries.

The composition of the single screw extruder: mainly consists of servo motor, reduction box, screw cylinder, nozzle head, filter air, heating and cooling system, touch screen, and SPS control. It is the extrusion host to form.

• What are the reasons why the main engine of the single screw extruder cannot be started and the solutions?

• What are the reasons and solutions for the high inlet flow of the single screw extruder?

• What is the design concept of the single screw extruder?

What are the reasons why the main engine of the single screw extruder cannot be started and the solutions?

1. Reasons:

(1) The driving program of the single screw extruder is wrong.

(2) There is a problem with the main engine thread and whether the fuse is blown.

(3) The locking device for the single screw extruder and the main engine works.

2. Treatment:

(1) Check the program of the insert extruder and restart in the correct order.

(2) Check the main engine circuit.

(3) Check whether the lubricating oil pump has started and check the status of the locking device concerning the main engine. The oil pump cannot be turned on and the engine cannot be turned on.

(4) The inverter has not discharged the induction current, turn off the main power supply and wait five minutes before starting.

(5) Check if the emergency button of the single screw extruder has been reset.

What are the reasons and solutions for the high inlet flow of the single screw extruder?

1. Reasons: (1) The single screw extruder has an insufficient heating time and a large torque. (2) A certain section of the heating does not work.

2. Treatment method: (1) Use the handwheel when driving the single screw extruder. If it is not easy, extend the heating time or check that the heaters of the individual sections work properly.

The main engine makes an abnormal noise:

1. Reasons: (1) Main engine stock damaged. (2) A specific SCR in the SCR DC power supply of the main engine is damaged.

2. Treatment method: (1) Replace the main engine stock of the single screw extruder. (2) Check the thyristor alignment and replace the thyristor component if necessary.

What is the design concept of the single screw extruder?

1. High-speed and high-Yield extrusion based on high quality.

2. The design concept of low-temperature plasticization ensures the extrusion of high-quality products.

3. The two-stage overall design of the single screw extruder reinforces the plasticization function to ensure the adjustment of the high-performance extrusion.

4. Special barrier, comprehensive mixing design to ensure the mixing effect of materials.

5. High torque drop, extra-large pressure bearing.

6. Gears and shafts are made of high-strength alloy steel, cooled, and chipped.

7. High hardness, high finish, extremely quiet.

8. PLC-intelligent control can realize the connection between main and auxiliary machines.

9. The easy-to-monitor human-machine interface makes it easy to understand the processing and machine status.

10. The control method (temperature device) can be changed if necessary.

11. The material is 38CrMoAL/A nitric treatment, wear-resistant.

12 Strict temperature control accuracy, combined with air cooling and water cooling.

13. The single screw extruder has a unique inlet design and complete water cooling.

14. An single screw extruder with a grooved surface of the lower shell has an improved feed function that guarantees a high speed and a high yield of extrusion.

The single screw extruder is increasingly used in industrial production.Nanjing JlEYA has committed itself to offering the best-suited single screw extruders at a reasonable price, and all that is necessary to meet the needs of the customer.

PVC compounding extruder is divided into RPVC pipe and SPVC pipe, RPVC pipe is easy to cut, welding, bonding, heating can be bent and therefore very easy to install and use. SPVC pipe has excellent chemical stability excellent electrical insulation and good flexibility and colorability this pipe is often used to replace rubber pipe to transport liquid and corrosive media also used as cable casing and wire insulation pipe, etc. So how do choose raw materials and the operation of PVC compounding extruder? The following is a detailed introduction

 

Here is the content list:

• Raw material selection

• Safety operating procedures

 

Raw material selection

PVC compounding extruder in the production of hard pipe resin should be selected from the lower polymerization degree of SG-5 resin polymerization degree of the higher its physical and mechanical properties and heat resistance is better, but the resin liquidity is poor to bring some difficulties in processing, so generally choose viscosity of 1.7 ~ 1.8 × 10-3Pa-s SG-5 resin is appropriate. Hard pipe generally uses lead-based stabilizers whose thermal stability is good commonly used trisodium lead but its lubricity is poor usually and good lubricity of lead, barium soap type and use. Processing hard tube lubricant selection and use are very important to consider both internal lubrication to reduce intermolecular forces to reduce the viscosity of the melt are conducive to molding and to consider external lubrication to prevent the melt and hot metal adhesion to make the product surface shiny. Internal lubrication is generally used metal soap type external lubrication with low melting point wax. Filler mainly with calcium carbonate and barium barite powder calcium carbonate to make the pipe surface performance of good barium can improve the molding of the pipe easy to shape both can reduce costs but the amount of too much will affect the performance of the pipe pressure pipe and corrosion-resistant pipe is best not to add or add less filler.

 

Safety operating procedures

1. Personnel without induction test and operation training cannot operate the extruder independently. 

2. People who have poor eyesight and slow response can not be on duty to operate. 

3. Before starting the machine to do a good job of environmental health around the PVC compounding extruder equipment, equipment around the pile of items not related to production. 

4. Check the safety settings of the extruder before production for damage and test whether it can work effectively. Check whether the connection bolts are loose and whether the safety guards are firm. 

5. Check the lubrication parts, remove the dirt, and refill the lubricant. 

6. PVC compounding extruder barrel and die heating constant temperature time to ensure that the material temperature does not reach the process requirements when driving production. 

7. Before starting the screw drive motor to use the hand plate support V pulley, should be flexible rotation, no blocking phenomenon; then start the lubricating oil pump work 3min before starting the screw rotation at low speed. 

8. Screw airlift time should not exceed 2 ~ 3min. 

9. PVC compounding extruder barrel before adding material to check the barrel, hopper, there is no foreign matter; raw materials should be free of metal, sand, and other impurities to Prevent damage to the screw. 

10. The screw starts, the transmission parts work sound normal, the main motor current within the allowable rated value, before allowing the barrel to add material, adding material should first be a small amount of evenly added material. 

11. When adjusting the die gap or clearing the dirty material, the operator should wear gloves and not face the barrel and die to prevent the molten material from spraying out of the die and scalding the body. 

12. Extruder driving operation is not allowed to repair, and no one is allowed to do any work on the equipment at this time. 

13. In case of the following phenomena, should be an emergency stop. 

Bearing parts of the high temperature, lubricating oil (grease) out; motor odor, smoke, or shell temperature is too high; speed box lubricating oil temperature, smoke; transmission parts emit irregular abnormal sound; machine work produces violent vibration; screw suddenly stop rotating.

14. PVC compounding extruder equipment on the safety cover and the location of the safety alarm device is not allowed to change at will, not to mention artificially caused by the malfunction. 

15. Find that the equipment leakage, oil leakage phenomenon should be timely maintenance troubleshooting, no water, oil flow around the machine.

 

If you have questions about how to use the PVC composite extruder, you can contact us on the official website. We are happy to answer for you.

The structure of the engineering plastic twin screw extruder barrel is basically similar to that of the single-screw extruder screw barrel. From the appearance structure, the twin-screw extruder barrel is also divided into an integral barrel and a segmented barrel. The engineering plastic twin screw extruder is an upgrade of the single screw extruder, which has also greatly improved the efficiency of use.

• What are the reasons why people choose engineering plastic twin screw extruder?

• What is the workflow of engineering plastic twin screw extruder?

• What are the essential devices in the engineering plastic twin screw extruder?

What are the reasons why people choose engineering plastic twin screw extruder?

1. Improve labor efficiency

When the equipment is repaired, engineering plastic twin screw extruder only needs to loosen a few bolts, turn the worm gear box handle device to lift the upper part of the barrel to open the entire barrel, and then perform repairs. This not only shortens the maintenance time, but also reduces the labor intensity.

2. High torque and high speed

The development trend of engineering plastic twin screw extruder in the world is towards high torque, high speed, and low energy consumption. The effect of high speed is high productivity. engineering plastic twin screw extruder belongs to this category, and its speed can reach 500 rpm. Therefore, it has unique advantages in processing high-viscosity, heat-sensitive materials.

3. Wide range of applications

engineering plastic twin screw extruder has a wide range of applications and can be applied to the processing of a variety of materials

4. High output, high quality

engineering plastic twin screw extruder has other advantages of ordinary extruder, and can achieve high output, high quality and high efficiency.

What is the workflow of engineering plastic twin screw extruder?

The engineering plastic twin screw extruder used for profile extrusion is usually tightly meshed and rotated in different directions, although a few also use co-rotating twin screw extruders, generally operating at a relatively low screw speed, about 10 r/ min. The high-speed meshing co-rotating engineering plastic twin screw extruder is used for compounding, venting or as a continuous chemical reactor. The maximum screw speed of this type of extruder is 300-600r/min. Non-intermeshing extruder is used for mixing, venting and chemical reaction. Its conveying mechanism is quite different from intermeshing extruder, which is closer to the conveying mechanism of single screw extruder, although there are essential differences between the two.

What are the essential devices in the engineering plastic twin screw extruder?

Among the straightening devices used in engineering plastic twin screw extruder, the most common one is eccentric, and various types of bending of the core are one of the important reasons for the insulation eccentricity. In sheath extrusion, scratches on the sheath surface are often caused by the bending of the cable core. Therefore, the straightening device in various engineering plastic twin screw extruder is indispensable. The main types of straightening devices are: drum type (divided into horizontal and vertical); pulley type (divided into single pulley and pulley block); winch type, which has multiple functions such as dragging, straightening, and tension stabilization; Press wheel type (divided into horizontal type and vertical type), etc.

The engineering plastic twin screw extruders are used more and more widely in daily life, but its quality has a great influence on the experience of use. Nanjing JlEYA has focused on the production and development of engineering plastic twin screw extruders for more than several years, and they have always put the needs of customers as their top priority.

When the single screw extruder is in the extrusion molding process, its extruder screw is divided into 3 sections: feeding section (feeding section), melting section (compression section), metering section (homogenization section), these three sections Correspondingly, three functional areas are composed of materials: solid conveying area, material plasticizing area, and melt conveying area. Each area has different temperature requirements, and specific problems should be analyzed in detail. The temperature of the single screw extruder will be briefly introduced below.

• What is the general temperature of the solid conveying zone in a single screw extruder?

• What is the general temperature in the plasticizing zone of the material in a single screw extruder?

• What is the general temperature of the melt conveying zone in a single screw extruder?

What is the general temperature of the solid conveying zone in a single screw extruder?

The temperature of the barrel in the solid conveying zone of the single screw extruder is generally controlled at 100~1400C. If the feeding temperature is too low, the solid conveying zone will be extended, reducing the length of the plasticizing zone and the melt conveying zone, which will cause poor plasticization of the single screw extruder product and affect product quality.

What is the general temperature in the plasticizing zone of the material in a single screw extruder?

The temperature of the material plasticizing zone in the single screw extruder is controlled at 170~1900C. Controlling the vacuum degree of this section is an important process index. If the vacuum degree is low, it will affect the exhaust effect, resulting in bubbles in the pipe, and seriously reducing the mechanical properties of the pipe. In order to make the gas inside the material easily escape, the plasticization degree of the material in this section should be controlled not to be too high, and the exhaust pipe of the single screw extruder should be cleaned frequently to avoid blockage. The vacuum degree of the barrel is generally 0.08~0.09MPa.

What is the general temperature of the melt conveying zone in a single screw extruder?

The temperature of the melt conveying zone in the single screw extruder should be slightly lower, generally 160~1800C. Increasing the screw speed in this section, reducing the head resistance and increasing the pressure in the plasticizing zone are all conducive to the improvement of the conveying rate. For heat-sensitive plastics such as PVC, the residence time should not be too long in this section. The screw speed is generally 20 ~30r/min. The head of the single screw extruder is an important part of extruded product molding. Its function is to generate a higher melt pressure and make the melt shape into a desired shape. The process parameters of each part of the single screw extruder are: die connector temperature 1650C, die temperature 1700C, 1700C, 1650C, 1800C, 1900C.

This is some information related to the use of single screw extruders. The use of single screw extruders is also closely related to the quality of its products. If you need more information, please contact Nanjing JlEYA.

The Underwater pelletizing machine cuts pellets on the plastic steel ejection surface without centrifugal action to eject them, but direct water pressure flows through the nozzle surface to drain.

• What is contained in the extrusion system of the Underwater pelletizing machine?

• What is the use of the Underwater pelletizing machine?

• What are the causes and solutions for the high melting of the Underwater pelletizing machine?

What is contained in the extrusion system of the Underwater pelletizing machine?

The extrusion system includes a snail, a cylinder, a funnel, a nozzle, and a nozzle. Through the extrusion system, the plastic is plasticized into a uniform melt and continuously extruded by the screw under the resulting pressure.

(1) Screw: It is the most important part of the Underwater pelletizing machine. It is directly related to the scope and productivity of the extruder. It consists of high-strength corrosion-resistant alloy steel.

(2) Cylinders: The cylinder is a metal cylinder that is generally made of alloy steel or composite steel tubes clad with alloy steel, heat resistant, high-pressure resistant, strong, wear-resistant, and corrosion-resistant. The cylinder and the screw are matched to each other to realize the crushing, grinding, melting, plasticization, suction, and compaction of the plastic as well as the continuous and uniform supply of the rubber material to the molding system. In general, the barrel length of an Underwater pelletizing machine is 15-30-fold its diameter, so that the plastic is completely heated and plasticized.

What is the use of the Underwater pelletizing machine?

Underwater pelletizing machines can be used for chemical fertilizers, white soot, inorganic salts, chlorinated isocyanic acid, bleaching powder, pesticides, oxides, etc. as well as for industrial recycling dust: such as cast iron dust, lead, zinc, aluminum dust, converter dust, filter dust, grinding dust, etc. The material is forced to be pressed and molded by mechanical pressure without adding a net, and the purity of the product is guaranteed. The process process process is short, energy consumption is low, and performance high. The dry powder is directly granulated without a subsequent drying process, which is more conducive to the connection and transformation of the existing production process. The granular strength is high and the increase in bulk density is more significant than in other granulation processes. The Underwater pelletizing machine is particularly suitable for occasions to increase the specific weight of the product collection. The operating flexibility is great, the range of applications is wide and the crushing force can be adjusted by hydraulic pressure.

What are the causes and solutions for the high melting of the Underwater pelletizing machine?

Causes analysis: high filter masks, low melting index of polypropylene powder and high feed volume, low temperature of each section of the Underwater pelletizing machine results in the material being incompletely melted, and a low opening rate of the template impede the extrusion of the nozzle head material, etc. The reasons may cause the melting pressure to be too high.

Solution: If the Underwater pelletizing machine produces products with a low melting index, a filter with a low mesh width should be used and the throttle opening should be enlarged to reduce backpressure; the filter should be replaced in time and the quality of different additives and polypropylene powder should be monitored. Contains medium ash. Reduce the feed load. Without compromising the quality of the extruded product, increase the temperature of each section of the cylinder to increase the temperature of the polypropylene melt and increase the flow capacity of the material. After the extruder has been stopped, increase the temperature of the head of the Underwater pelletizing machine and keep it at a constant temperature for a while and rinse and then thoroughly clean the template.

The underwater pelletizing machine have been used in many fields Nanjing JlEYA maintains close relationships with customers in underwater pelletizing machine industry, and is committed to strengthening production and operation, improving quality and safety.

The engineering plastic twin screw extruder was developed based on a single screw extruder. Due to its good feed performance, mixing and plasticization performance, suction performance, and extrusion stability, it is often used in extruded products.

• What are the advantages of engineering plastic twin screw extruders?

• What role do pre-heaters play in the use of engineering plastic twin screw extruders?

• What is the reason for the "fault" of the exhaust air opening of the engineering plastic twin screw extruder?

What are the advantages of engineering plastic twin screw extruders?

1. wear

By simply opening the engineering plastic twin screw extruder, the wear level of the threaded parts and the inner sockets of the cylinder can be determined at any time, so that we need to carry out effective maintenance or exchange. It is not detected if there is a problem with the extruded product causing unnecessary waste.

2. Reduce production costs

When a engineering plastic twin screw extruder is made of technical plastic Masterbatch, it is often necessary to change the color. It is necessary to change the product.

Simply open the open editing area within a few minutes. In addition, the mixing process can be performed by observing the melting profile on the entire screw. analysis. When changing the color of an ordinary engineering plastic twin screw extruder, a large amount of cleaning material is needed to clean the machine, which is time and energy consuming and wastes raw materials. The split engineering plastic twin screw extruder can solve this problem. When changing color, it takes only a few minutes to quickly open the barrel for manual cleaning, so that no or fewer cleaning agents can be used, which saves costs.

What role do pre-heaters play in the use of engineering plastic twin screw extruders?

A pre-heating of the cable core is required for the use of an engineering plastic twin screw extruder. The presence of pores shall not be permitted for the insulating layer, in particular the thin insulating layer. The wire core can be completely removed from the water and oil surface by high-temperature preheating before crushing. In the case of coat extrusion, its main function is to dry the cable core to prevent the possibility of pores in the coat due to moisture (or moisture around the cushion layer). By preheating, the residual pressure of the plastic can also be prevented by discouragement during extrusion. During the plastic extrusion of the processor, preheating can eliminate the large temperature difference that occurs when the cold wire enters the high-temperature nozzle and the nozzle is in contact with the plastic, thereby avoiding the fluctuation of the plastic temperature and causing the fluctuation of the extrusion pressure. This stabilizes the extrusion volume and ensures the extrusion quality. The technical plastic engineering plastic twin screw extruder uses an electric radiator preheating device that requires sufficient capacity and guarantees rapid heating so that the core preheating and drying efficiency of the cable core is high. The pre-heat temperature is limited by the deflection speed and generally corresponds to the temperature of the machine part.

What is the reason for the "fault" of the exhaust air opening of the engineering plastic twin screw extruder?

The temperature of the machine part is low and the pressure of the machine part is too high.

engineering plastic twin screw extruder The engineering plastic twin screw extruder used for profile extrusion is usually narrow-meshed and rotates in different directions, but a few also use simultaneous engineering plastic twin screw extruders, which usually work with relatively low screw speed. About ten U/min.

The rapidly combining, simultaneous engineering plastic twin screw extruder is used for composting, venting or as a continuous chemical reactor. The maximum snail speed of this extruder type is 300-600 U/min. The non-interactive extruder is used for mixing, venting, and chemical reaction. Its conveyor mechanism is very different from the interlocking extruder, which is closer to the conveyor mechanism of a single screw extruder.

These are related practices for using engineering plastic twin screw extruders. If you want to get more information about the engineering plastic twin screw extruders, please connect Nanjing JlEYA, and they will tell you more about it.

Degradable plastics refer to a class of plastics whose various properties can meet the requirements of use, remain unchanged during the shelf life, and can be degraded into environmentally harmless substances under natural environment conditions after use. Therefore, it is also called environmentally degradable plastic.
There are a variety of new plastics: photodegradable plastics, biodegradable plastics, light/oxidative/biodegradable plastics, carbon dioxide-based biodegradable plastics, thermoplastic starch resin degradable plastics.
There are two main areas for the use of degradable plastics: one is the area where ordinary plastics were originally used. In these areas, the difficulty of collecting used or post-consumer plastic products will cause harm to the environment, such as agricultural mulch and single-use plastic packaging, and the second is areas where plastics are used instead of other materials. The use of degradable plastics in these areas can bring convenience, such as ball tacks for golf courses, and seedling fixing materials for tropical rainforest afforestation.
Specific applications are:
1.Agriculture, forestry and fishery, plastic film, water-retaining materials, seedling pots, seedbeds, rope nets, slow-release materials for pesticides and agricultural fertilizers.
2.Packaging industry, shopping bags, garbage bags, compost bags, disposable lunch boxes, instant noodle bowls, buffer packaging materials.
3.Sporting goods, golf tacks and tees
4.Hygiene products, women's hygiene products, baby diapers, medical mattresses, disposable haircuts.
5.Medical materials, bandages, clips, small sticks for cotton swabs, gloves, drug release materials, and surgical sutures and fracture fixation materials.
Nanjing Jieya also manufactures twin screw compounding extruder for bio-degradable material. We warmly welcome your inquiry.

The extrusion technology used by the single screw extruder is making waves in the food production industry. We know that single screw extruder can mass produce enterprise products of various shapes and textures. It allows a seamless and continuous operation process, which means that this means lower costs and higher production and sales.

• What are the reasons and solutions for the poor discharge or blockage of the single screw extruder head?

• What is the importance of single screw extruder temperature control?

• What is the importance of single screw extruder speed control?

What are the reasons and solutions for the poor discharge or blockage of the single screw extruder head?

1. Reasons: (1) A certain section of the heater does not work, and the material is poorly plasticized. (2) The operating temperature is set too low, or the molecular weight distribution of the plastic is wide and unstable. (3) There may be foreign objects in the single screw extruder that are not easy to melt.

2. Treatment method: (1) Check the heater and replace it if necessary. (2) Verify the set temperature of each section, negotiate with the technician if necessary, and increase the temperature set value. (3) Clean and check the extrusion system and head of the single screw extruder.

What is the importance of single screw extruder temperature control?

Temperature control refers to the temperature of the single screw extruder during plastic extrusion, including the temperature control of the barrel, die and transition body. These temperature controls are related to the viscosity of the material, the sensitivity to temperature, and the aggregation state of the polymer. In general, the temperature of the die head and transition body of single screw extruder is low for medium and low viscosity materials, and the temperature of die head and transition body for high viscosity materials is high, and the fluidity is good.

What is the importance of single screw extruder speed control?

Speed control means that for single screw extrude processing, if the screw speed increases, the shear rate increases. Thermoplastic melts are mostly non-Newtonian pseudoplastic fluids, and their viscosity decreases with the increase of shear rate, and fluidity Increasing the extrusion output also increases. However, if the shear rate is too large, the melt viscosity is too low, which will cause difficulties in the production and operation of single screw extrude. At the same time, the low-viscosity melt will flow backwards under the action of the screw back pressure, and the leakage flow will increase significantly, which will affect the output to a certain extent. , Again, the screw may even slip at high speeds, so the screw speed should be controlled within a certain range. In addition, in the production process of single screw extrude, the screw speed should be kept as stable as possible to avoid fast and slow. Otherwise, it will cause uneven discharge due to excessive changes in the melt viscosity of the material, which will affect normal production.

Nanjing JlEYA is a single screw extruder manufacturer established for more than five years. We work with customers from design to completion to ensure that all technical requirements are met.

twin screw extruder for sale, Quality plastic pellet Polymer compounding parallel co-rotating twin screw extruder on sale of Nanjing Chuangbo Machinery Co.,LTD from China. ... PP PE PC PA ABS PVC WPC TPU TPR: Screw Design:: Double-screw: Voltage:: 380V or as customerized: Function::

Labour day also known as May Day, originated in the 19th century to observe

The PEARLO¿¿ underwater pelletizer has been designed to process a wide range of polymers and thermoplastics. PEARLO¿¿ works perfectly with our process water system PURO¿¿ and pellet dryer CYCLO¿¿ and produces mostly spherical pellets. This efficient and flexible system is applied in the production of raw materials,compounds ...

Our laboratory twin-screw extruder is researched and developed for universities, colleges, scientific research institution and large and medium food enterprises. 1. Main features: 1. High strength building block …

Chemglass. Stainless steel transistion adapter from beaded pipe on the inlet/outlet of the reactor to M16 x 1 or M30 x 1.5 male. Used to connect fluid transfer hose to the vessel. Adapters require the beaded pipe couplings for connection to the …

WPC granulate has consistent running properties on the machine, facilitating a higher output. Due to compounding, the density of the material is higher compared to direct extrusion. Granulated WPC and the end products …

Search for used underwater pelletizing systems. Find Kairong and Haisi for sale on Machinio. ... TPU EVA Compounds Plastic Underwater Pelletizing System Technical …

Pelletizing Line Plastic Pelletizing Machine Factory Supply Attractive Price PP PE Pelletizing Line Pellet Machine Extruder Recycled Plastic Extruder US