PVC compounding extruder is divided into RPVC pipe and SPVC pipe, RPVC pipe is easy to cut, welding, bonding, heating can be bent and therefore very easy to install and use. SPVC pipe has excellent chemical stability excellent electrical insulation and good flexibility and colorability this pipe is often used to replace rubber pipe to transport liquid and corrosive media also used as cable casing and wire insulation pipe, etc. So how do choose raw materials and the operation of PVC compounding extruder? The following is a detailed introduction
Here is the content list:
Raw material selection
Safety operating procedures
PVC compounding extruder in the production of hard pipe resin should be selected from the lower polymerization degree of SG-5 resin polymerization degree of the higher its physical and mechanical properties and heat resistance is better, but the resin liquidity is poor to bring some difficulties in processing, so generally choose viscosity of 1.7 ~ 1.8 × 10-3Pa-s SG-5 resin is appropriate. Hard pipe generally uses lead-based stabilizers whose thermal stability is good commonly used trisodium lead but its lubricity is poor usually and good lubricity of lead, barium soap type and use. Processing hard tube lubricant selection and use are very important to consider both internal lubrication to reduce intermolecular forces to reduce the viscosity of the melt are conducive to molding and to consider external lubrication to prevent the melt and hot metal adhesion to make the product surface shiny. Internal lubrication is generally used metal soap type external lubrication with low melting point wax. Filler mainly with calcium carbonate and barium barite powder calcium carbonate to make the pipe surface performance of good barium can improve the molding of the pipe easy to shape both can reduce costs but the amount of too much will affect the performance of the pipe pressure pipe and corrosion-resistant pipe is best not to add or add less filler.
1. Personnel without induction test and operation training cannot operate the extruder independently.
2. People who have poor eyesight and slow response can not be on duty to operate.
3. Before starting the machine to do a good job of environmental health around the PVC compounding extruder equipment, equipment around the pile of items not related to production.
4. Check the safety settings of the extruder before production for damage and test whether it can work effectively. Check whether the connection bolts are loose and whether the safety guards are firm.
5. Check the lubrication parts, remove the dirt, and refill the lubricant.
6. PVC compounding extruder barrel and die heating constant temperature time to ensure that the material temperature does not reach the process requirements when driving production.
7. Before starting the screw drive motor to use the hand plate support V pulley, should be flexible rotation, no blocking phenomenon; then start the lubricating oil pump work 3min before starting the screw rotation at low speed.
8. Screw airlift time should not exceed 2 ~ 3min.
9. PVC compounding extruder barrel before adding material to check the barrel, hopper, there is no foreign matter; raw materials should be free of metal, sand, and other impurities to Prevent damage to the screw.
10. The screw starts, the transmission parts work sound normal, the main motor current within the allowable rated value, before allowing the barrel to add material, adding material should first be a small amount of evenly added material.
11. When adjusting the die gap or clearing the dirty material, the operator should wear gloves and not face the barrel and die to prevent the molten material from spraying out of the die and scalding the body.
12. Extruder driving operation is not allowed to repair, and no one is allowed to do any work on the equipment at this time.
13. In case of the following phenomena, should be an emergency stop.
Bearing parts of the high temperature, lubricating oil (grease) out; motor odor, smoke, or shell temperature is too high; speed box lubricating oil temperature, smoke; transmission parts emit irregular abnormal sound; machine work produces violent vibration; screw suddenly stop rotating.
14. PVC compounding extruder equipment on the safety cover and the location of the safety alarm device is not allowed to change at will, not to mention artificially caused by the malfunction.
15. Find that the equipment leakage, oil leakage phenomenon should be timely maintenance troubleshooting, no water, oil flow around the machine.
If you have questions about how to use the PVC composite extruder, you can contact us on the official website. We are happy to answer for you.
Nanjing JIEYA attend Chinaplas 2021 held in Shenzhen. We sincerely welcome your visiting.
Our booth no.: 7Q25
Time: April 13-16, 2021
Address: Shenzhen World Exhibition Center
Look forward to meet you at there.
![]() | ![]() |
The engineering plastic twin screw extruder was developed based on a single screw extruder. Due to its good feed performance, mixing and plasticization performance, suction performance, and extrusion stability, it is often used in extruded products.
What are the advantages of engineering plastic twin screw extruders?
What role do pre-heaters play in the use of engineering plastic twin screw extruders?
What is the reason for the "fault" of the exhaust air opening of the engineering plastic twin screw extruder?
1. wear
By simply opening the engineering plastic twin screw extruder, the wear level of the threaded parts and the inner sockets of the cylinder can be determined at any time, so that we need to carry out effective maintenance or exchange. It is not detected if there is a problem with the extruded product causing unnecessary waste.
2. Reduce production costs
When a engineering plastic twin screw extruder is made of technical plastic Masterbatch, it is often necessary to change the color. It is necessary to change the product.
Simply open the open editing area within a few minutes. In addition, the mixing process can be performed by observing the melting profile on the entire screw. analysis. When changing the color of an ordinary engineering plastic twin screw extruder, a large amount of cleaning material is needed to clean the machine, which is time and energy consuming and wastes raw materials. The split engineering plastic twin screw extruder can solve this problem. When changing color, it takes only a few minutes to quickly open the barrel for manual cleaning, so that no or fewer cleaning agents can be used, which saves costs.
A pre-heating of the cable core is required for the use of an engineering plastic twin screw extruder. The presence of pores shall not be permitted for the insulating layer, in particular the thin insulating layer. The wire core can be completely removed from the water and oil surface by high-temperature preheating before crushing. In the case of coat extrusion, its main function is to dry the cable core to prevent the possibility of pores in the coat due to moisture (or moisture around the cushion layer). By preheating, the residual pressure of the plastic can also be prevented by discouragement during extrusion. During the plastic extrusion of the processor, preheating can eliminate the large temperature difference that occurs when the cold wire enters the high-temperature nozzle and the nozzle is in contact with the plastic, thereby avoiding the fluctuation of the plastic temperature and causing the fluctuation of the extrusion pressure. This stabilizes the extrusion volume and ensures the extrusion quality. The technical plastic engineering plastic twin screw extruder uses an electric radiator preheating device that requires sufficient capacity and guarantees rapid heating so that the core preheating and drying efficiency of the cable core is high. The pre-heat temperature is limited by the deflection speed and generally corresponds to the temperature of the machine part.
The temperature of the machine part is low and the pressure of the machine part is too high.
engineering plastic twin screw extruder The engineering plastic twin screw extruder used for profile extrusion is usually narrow-meshed and rotates in different directions, but a few also use simultaneous engineering plastic twin screw extruders, which usually work with relatively low screw speed. About ten U/min.
The rapidly combining, simultaneous engineering plastic twin screw extruder is used for composting, venting or as a continuous chemical reactor. The maximum snail speed of this extruder type is 300-600 U/min. The non-interactive extruder is used for mixing, venting, and chemical reaction. Its conveyor mechanism is very different from the interlocking extruder, which is closer to the conveyor mechanism of a single screw extruder.
These are related practices for using engineering plastic twin screw extruders. If you want to get more information about the engineering plastic twin screw extruders, please connect Nanjing JlEYA, and they will tell you more about it.
Malfunctions that are caused by inadequate or improper maintenance can result in high repair costs and unnecessarily long gearbox down times. Regular servicing and inspection work are therefore imperative!
All servicing and repair work is only allowed to be performed with the gearbox stationary and by trained,authorized and appropriately instructed personnel.
Refilling lubrication oil
The oil level is to be checked regularly.It must never be below the bottom mark. In the case that the oil level drops below the minimum,it is imperative that the lubricant is topped up. The oil is only allowed to be topped up with the drive units shut down. A funnel with a filter is to be used for toppcng up (filter mesh 40um). The gearbox is always to be filled with the same type of oil as used previously It is not allowed to mix different oils or oils from different manufacturers.
Changing oil
The effectiveness of the oil reduces with increasing use due to soiling (foreign bodies and water) and chemical changes(ageing products). When the soiling and/or ageing is/are excessive, it is necessary to change the oil. Regular oil analyses provide information on the effectiveness of the gearbox oils. For larger quantities of oil it is recommended to make oil changes dependent on the results of an oil analysis.A missed oil change increases the risk of damage and can result in premature failure of the gearbox.
The first oil change should be made at approx.2500 perating hours.Subsequent oil changes depend on the state of the oil and are to be performed every 4,000 to 6,000 operating hours, however at the latest after one year.
The gear box is the core part of the twin screw extruders, we shall pay attention to its maintenance for long servicelife.
The twin screw extruder's standard equipment includes a sturdy base frame dedicated to housing the temperature control unit and oil lubrication system. The equipment features advanced control software for seamless integration into digital factories, ready for Industry 4.0, greatly improving ease of use. The following is a detailed description of the operating procedures of the twin screw extruder.
Here is the content list:
l Start up operation
l Stop the machine
l Precautions
Start up operation
1.Close the power main gate of the twin screw extruder.
2. Turn on the power at the operation panel: Press and hold the power button clockwise to turn and then release.
3. Set the temperature of each temperature zone: for example, a zone temperature according to the process requirements set the corresponding temperature, press the set button, and then adjust the up and down arrows to the desired temperature, press the set button.
4. Set the feeding rate: according to the process, requirements can be fed rate between 0 ~ 10 to set.
5. Set the host speed of the twin screw extruder: set the host speed between 0~30 according to the process requirements.
6. Add cooling water to the cooling tank.
7. In turn on the fan: press the operation button on the operation panel.
8. When you need to start the operation of the vacuum pump, you can start the vacuum pump.
9. Turn on the cutter switch.
1. Twin screw extruder normal stopping sequence: stop the feeder: close the vacuum line valve, open the vacuum chamber on the cover; gradually reduce the main screw speed; shut down the pelletizer and other auxiliary equipment: off the motor, each external water inlet valve.
2. Twin screw extruder emergency stop: (1) in case of an emergency need to stop the host, you can quickly press the electrical control cabinet red emergency stop button, and the host and the feed speed knob back to zero, and then the total power switch off. After eliminating the fault, you can restart the machine again in normal driving order. (2) encounter equipment automatic protection trip stop: need to set the various parameters knob to zero, and then reset the parameters, press the reset button and start the machine again.
1. The normal production of the first shift machine, be sure to first check whether the barrel, hopper seal is the original closed kind, such as changes or damage, should check the hopper, the machine inside the Jane there are no foreign objects.
2. Pay attention to the screw to start at a low speed, the air time can not exceed 3min.
3. Must pay attention to check the purity of each batch of material, do not allow any impurities mixed into the material.
4. The beginning of the material to pay attention to the first small amount, evenly added material, while paying attention to observe the current meter (torque meter) pointer changes.
For granular material, use metering to add material. When you first start to feed production, be sure to pay attention to the extruder production work overload phenomenon. After the forming die lip out of the material, and then gradually increase the screw speed as appropriate.
5. Often check the working condition of the motor carbon brush, abnormalities should be replaced or adjusted promptly.
6. The screw cleaning work is not allowed to use steel tools scraping material, the application of copper brush, shovel cleaning.
7. When the process temperature is suspected of displaying problems on the instrument, use mercury temperature, meter actual measurement of the machine Jane, and molding mold degree. Refer to the mercury temperature measured temperature, adjust the calibration instrument to show the temperature.
If you still have questions, you can consult our company. Our company's website is https://www.njjyextrusion.com/
Today, we loaded 2x40HQ export to Vietnam.
One is SHJ-50 twin screw extruder, the other is SHJ-72 twin screw extruders. Both extruders are used for making filler masterbatch.
Nanjing Jieya is a leading manufacturer of twin screw compounding extruders with over 20 years experience. We will offer you the top quality with best price.
We warmly welcome your inquiry.
With the development of modern industry, the underwater pelletizing machine has become an important production equipment used in all aspects of production.
What is the working principle of the underwater pelletizing machine?
What is the operating procedure of the underwater pelletizing machine?
What are the reasons why people choose underwater pelletizing machine?
The material using the underwater pelletizing machine will pass through the feeding port, and under the action of the rotating screw, it will be rolled into a dough and roll forward along the screw groove. Due to the shear, compression and agitation of the screw, the material will be further mixed and plasticized. , The temperature and pressure gradually increase, showing a state of viscous flow, and passing through the machine head with a certain pressure and temperature, and finally a product of the desired shape is obtained.
(1) Check the rotation direction of the impeller of the underwater pelletizing machine. From the feed inlet, the impeller should turn counterclockwise, otherwise the motor connection should be adjusted.
(2) The starting sequence of the underwater pelletizing machine and the material conveying equipment is as follows:
Discharge belt conveyor→PL vertical impact crusher→feeding belt conveyor
The crusher must be started without load, and the material can only be fed after the crusher is running normally.
(3) The feed size is strictly in accordance with the feed size specified by the various models. It is forbidden to enter the underwater pelletizing machine with the size of the material larger than the specified size, otherwise it will cause the impeller imbalance and excessive wear of the impeller, and even block the impeller flow path and The central feed pipe prevents the crusher from working normally. When a large piece of material is found, it should be removed in time.
(4) When the discharge belt conveyor stops running, the feeding should be stopped immediately, so the discharge belt conveyor should be interlocked with the feeding system to open and stop. Otherwise, the impeller will be crushed and the motor will be burnt.
(5) The feeding of the underwater pelletizing machine should be uniform and continuous.
(6) During the operation of the underwater pelletizing machine, there must be no violent vibration or abnormal noise, otherwise, it should be stopped immediately for inspection, and the machine can only be driven in order after the fault is removed.
(7) The observation door should be sealed tightly during the working process of the underwater pelletizing machine.
The difference between the underwater pelletizing machine and other similar products is that it has a steady stream of water flowing through the mold surface, and it is in direct contact with the mold surface. The size of the pelletizing chamber is just enough to allow the pelletizing knife to rotate freely across the die surface without restricting the temperature of the water flow. The molten polymer has been extruded from the die, and the rotating knife cuts the pellets. And then the pellets are taken out of the pelletizing chamber by the temperature-regulated water and enter the centrifugal dryer. In the dryer of the underwater pelletizing machine, the water will be drained back to the storage tank, cooled and recycled; the pellets pass through the centrifugal dryer to remove the water.
This is how we see the irreplaceable role of underwater pelletizing machine in our daily lives and industrial production. Nanjing JlEYA, the pioneer of underwater pelletizing machine producing company in China, knows that every application is special. You can go and get more information about them