PVC compounding extruder is divided into two types of hard and soft RPVC pipes, RPVC pipes are chemically resistant and insulating, mainly transporting various fluids and used as wire sleeves, etc. SPVC pipes are manufactured by extruding PVC resin with a large amount of plasticizer and a certain amount of stabilizer and other additives after granulation. The following is a detailed description of the equipment functions of the PVC compounding extruder.
Here is the content list:
High Speed Mixer High-Speed Mixing
Accurate matching of feeding device
Water tank for pipe forming
Traction machine frequency conversion speed control
Automatic cutting
Unloading the material from the turning frame
Raw material intermixture is to feature PVC stabilizer, softener, inhibitor, and different auxiliary materials to the high-speed mixer in proportion and sequence to the method.
The PVC compounding extruder part is equipped with a quantitative feeding device to match the extrusion volume with the feeding volume to ensure stable extrusion of products. Due to the characteristics of the conical screw, the feeding section has a larger diameter, and the heat transfer area and sheer speed of the material are larger, which is contributive to the plasticization of the fabric and also the little diameter of the screw within the metering section reduces the warmth transfer space and also the sheer speed of the soften so that the melt can be extruded at a lower temperature. When the screw rotates in the barrel, the PVC mixture is plasticized and pushed to the head to achieve compaction, melting, mixing, and homogenization and to achieve the purpose of exhaust and dehydration. The feeding device and screw drive device adopt frequency conversion to realize synchronous speed regulation.
PVC compounding extruder dies head part of the compacted, molten, blended, and homogenized PVC has subsequent materials through the screw to the die head extrusion die head is the key component of pipe forming.
The vacuum shaping water tank of PVC compounding extruderis used for pipe shaping and cooling, the vacuum shaping water tank is equipped with vacuum system for shaping and cooling and water circulation system stainless steel box body circulating water spray cooling, the vacuum shaping water tank is equipped with front and rear moving device and left and right, high and low adjustment manual device.
The traction machine is used to continuously and automatically lead the cooled and hardened pipe from the head with frequency control.
The cutting machine is controlled by the travel switch according to the required length and then automatically cut and delay the turning frame to implement the flow of production, the cutting machine with a fixed-length work switch signal as a command to complete the whole process of cutting in the cutting process and pipe running synchronization cutting process is completed by electric and pneumatic drive, the cutting machine is equipped with a dust suction device to suck out the cutting debris and recycling.
Unloading the material from the turning frame
The material turning action is controlled by the cylinder through the air circuit to achieve the material turning frame is equipped with a limit device when the cutting saw cut off the pipe after the pipe continues to transport after a delay, the cylinder into the work of turning action to achieve the purpose of unloading. After unloading, it will be automatically reset after a delay of several seconds to wait for the next cycle.
Nanjing JlEYA is the leading manufacturer extruder manufacturer specializing in twin screw extruder, mini twin screw extruder, plastic extruder and parallel twin screw extruder in China, which is widely used in compounding, modification, polymerization, devolatilization, reaction, recycling, etc. After 17 years development, now we have 20,000 square meters workshop with annual sales over 300+ sets, export over 60 countries.
JIEYA has the most experienced technical core team, with extensive experience in system integration of the development manufacturing, materials processing, application technology andother fields.
Twin screw extruder is developed based on the single screw extruder, which has been widely used in the molding process of extruded products because of its good feeding performance, mixing and plasticizing performance, exhaust performance, and extrusion stability. So what are the advantages of a twin screw extruder? The following is a detailed introduction.
Here is the content list:
l Wear and tear
l Reduce production costs
l Increase output
l Improve labor efficiency
l High torque and high speed
Wear and tear
Since twin screw extruders are easy to open, the degree of wear of threaded elements and barrel bushings can be detected at any time, so that effective repair or replacement can be carried out. It is not necessary to find out only when there is a problem with the extruded product, which causes unnecessary waste.
Reduce production costs
When producing masterbatches on twin screw extruders, it's usually necessary to alter colors, and if a product amendment is critical, to open the open process space within several minutes, in addition to analyzing the mixing process by looking at the melt profile on the entire screw. The current common twin screw extruder needs to be cleared with a large amount of clearing material when changing colors, which is time consuming, power consuming, and a waste of raw material. The split twin screw extruder can solve this problem. When changing the color, it only takes a few minutes to quickly open the barrel for manual cleaning, so that no or less cleaning material can be used, saving costs.
Increase output
Twin screw snack extruders use side feeding technology to improve the integrity of the material and greatly increase production. The position and shape of the feed opening also have a great influence on feeding efficiency. With the same parameters, the output increases with an increase in the feed area. A rectangular cross section has a higher feed efficiency than a circular cross section for the same inlet area. The use of side by side twin screw feeds is also based on this consideration.
Improve labor efficiency
During equipment maintenance, ordinary twin screw extruders often have to remove the heating and cooling system before the screw can be withdrawn as a whole. In contrast, the split twin screw does not need to be opened by loosening a few bolts and turning the worm gearbox handle device to lift the upper half of the barrel, and then the entire barrel can be repaired. This shortens the maintenance time and reduces the labor intensity.
High torque and high speed
At present, the event trend of twin screw extruders within the world is to develop within the direction of high torsion, high speed, and low energy consumption, and also the impact of high speed is high productivity. The split twin screw extruder belongs to the current class, and its speed will reach and five hundred revolutions per minute. Therefore, its distinctive benefits in process high viscousness and warmth sensitive materials.
In the high speed, high torque core technology, asymmetric and symmetric high torque gearbox currently only Germany and Japan related manufacturers master the core technology, its speed can reach up to 1800 rpm or more, and domestic also master this core technology, such as Nanjing JlEYA extrusion company, is also currently one of the main choices of domestic high end material processing manufacturers, belongs to the domestic independent innovation national encouragement projects.
If you want to buy twin screw extruders, you can consider our cost effective products. We insist on the tenet of "quality first, customer first" and warmly welcome new and old customers to cooperate with us.
The company focuses on twin screw extruders, micro twin screw extruders, plastic extruders, parallel twin screw extruders, and other research and development and manufacturing as the core of the isotropic rotary twin screw mixing and extruding machine, the application range covers the mixing and modification of granulation, polymerization, deswelling, step molding, recycling, and other fields.
Nanjing Jieya is a professional manufacturer of twin screw compounding extruders since 2004. Our extruders series include SHJ series, HT series, JY series, SJ series, etc. Today we will tell you the differences between SHJ series twin screw extruders and HT series high torque twin screw extruders from three main points below:
1. Torque grade
The torque rating grade of our SHJ series twin screw extruder is T/A3≤8 while HT series is 9≤T/A3≤13.5. Our HT series adopt high torque gear box, which is suitable for customers that pursuit high efficiency machines.
2. Power transmission
SHJ series use clutch for power transmission while HT series use torque protector, for example, R+W brand, Bibby brand, etc.
3. Output
The output of HT series twin screw extruder is much higher than SHJ series.
So HT series can further improve the performance of extruders.But surely, price is higher than SHJ series.
A single-screw extruder consists of an Archimedes screw rotating in a heated barrel. It is widely used because of its simple structure, easy manufacturing, high processing efficiency, and low price, and is the most technically mature and used type of extruder at present. The following is a detailed introduction to single-screw extruders.
Here is the content list:
The design concept of a single-screw extruder
Single-screw extruder features
Uses of single screw extruder
(1) Single-screw extruders are high-speed, high-output extrusions based on high quality, and the design concept of low-temperature plasticization ensures the extrusion of high-quality products. Two-step overall design to strengthen the plasticizing function and ensure the adjustment of high-performance extrusion.
(2) A special barrier of the single-screw extruder, integrated mixing design to ensure material mixing effect and high torque output, extra-large thrust bearing.
(3) The gears and shafts of a single screw extruder are high-strength alloy steel, carburized, ground teeth treatment, high hardness, high finish, and ultra-low noise. PLC intelligent control, the linkage between main and auxiliary machines is possible.
(4) Single screw extruder easy to monitor human-machine interface, easy to understand the processing and machine status, and the control method (temperature control instrument) can be changed as needed.
(5) The material of the single screw extruder is 38CrMoAL/A nitride treatment, which is wear-resistant. It has a combination of air-cooled and water-cooled cooling for strict temperature precision control, and the unique air inlet design makes it a perfect water-cooling device.
(6)Single screw extruder with grooved surface feeding bottom sleeve of screw barrel has enhanced feeding function, which provides a guarantee for high speed and high output extrusion.
1. Hard gearbox, AC or DC stepless drive speed regulation.
2. New screw structure, melt and mix uniformly to ensure low melt temperature and high output
3. Screw barrel material adopts nitride steel 38CrMoAIA nitride treatment, and the surface alloy treatment has higher hardness.
4. Cast copper, cast aluminum heater, air-cooled and water-cooled according to requirements.
5. Advanced electrical control system of single screw
Pipe extrusion of single-screw extruder: it is suitable for PP-R pipe, PE gas pipe, PEX cross-linked pipe, aluminum-plastic composite pipe, ABS pipe, PVC pipe, HDPE silicon core pipe, and various co-extruded composite pipes.
Sheet and plate extrusion: applicable to PVC, PET, PS, PP, PC, and other profiles and plates extrusion. Extrusion of various other plastics such as silk, rod, etc.
Profile extrusion: adjusting the extruder speed and changing the structure of the extrusion screw can be applied to the production of various plastic profiles such as PVC, polyolefin, etc. Modified pelletizing: It is suitable for blending, modifying, and enhancing pelletizing of various plastics.
Nanjing JlEYA is a leading extruder manufacturer specializing in a twin-screw extruder, micro twin-screw extruder, plastic extruder, and parallel twin-screw extruder, which are widely used in compounding, modification, polymerization, devolatilization, reaction, recycling, and other fields. After 17 years of development for many years, now we have a 20,000 square meters plant, 300+ sets of annual sales, and export to more than 60 countries.
As common extruder equipment used in the plastic processing industry, single screw extruder is mainly used for extruding soft and hard PVC, polyethylene, and other thermoplastics, which can process many kinds of plastic products, such as blown film, extruded pipe, pressboard, drawn ribbon, etc. It can also be used for melt pelletizing. The plastic extruder has advanced design, high quality, good plasticization, low energy consumption, involute gear transmission, low noise, smooth operation, high load capacity, and long life. To have a long service life of the machine, maintenance measures are indispensable, the following is a detailed description of the single-screw extruder maintenance measures.
Here is the content list:
Daily maintenance.
Regular maintenance.
1. Because the electrical control system of single-screw extruder has high requirements for ambient temperature and dustproof, the electrical system should be separated from the production site, and install ventilation or ventilation fan, it is recommended that the electrical control cabinet in a simple room, keep the room clean, ventilation, so that the indoor temperature is not higher than 40 ℃.
2. Single-screw extruderis not allowed to run empty, so as not to roll the screw and machine simple hair. Host start idling is not allowed to exceed 100r / min; start the host first low speed, after starting the host to check for abnormal noises and then slowly increase the host speed to within the allowable range of the process (can be adjusted to the best state is good). When the new machine is breaking in, the current load should be at 60-70%, and the current in normal use should preferably not exceed 90%. Note: If an abnormal sound occurs when the extruder is running, it should be stopped immediately for inspection or repair.
3. Turn on the oil pump first and turn off the oil pump after shutting down the machine; keep the water pump working during the whole production process and do not stop the pump to avoid the barrel temperature rising and causing the material in the barrel to decompose and carbonize; the asbestos wind cover of the main motor fan needs to be cleaned often to avoid the dust sticking too much to block the wind cover and cause the motor to overheat and trip due to insufficient heat dissipation.
4. Clean up the dust and dirt, tools, and debris on the surface of the unit in time.
1.Regularly check the screws and other fasteners on the surface of the single-screw extruder unit for looseness and timely and proper tightening. The lubricant level of the transmission box should be added or replaced promptly (the dirt at the bottom of the oil tank should be cleaned regularly). For new machines generally, 3 months to replace the oil, after that every six months to a year. The oil filter and oil suction pipe should be cleaned regularly (once a month).
2. Single screw extruder gearbox maintenance and general standard reducer are the same. The main thing is to check the wear and failure of gears and bearings.
3, When reinstallation please note that A, B two screws must be in the original position, can not be replaced! After the installation of the new combination of the screw on the machine, you must first use the hand pan car, such as normal rotation before the low-speed start. Screw or barrel for a long time without use, there should be anti-rust and anti-fouling measures, the screw should be placed hanging. If the threaded block is with fire, the flame should be moved left and right, while burning to clean up, and can not burn too much (blue ringers red), not to mention the thread block into the water.
4. Regularly calibrate the temperature control instrument to check the correctness of its adjustment and the sensitivity of its control.
5. In the barrel with a cooling water tank, must be used distilled water to prevent the formation of scale blocking the cooling water channel in the barrel, resulting in temperature failure. Pay attention to the appropriate amount of water in use to prevent scaling. If the blockage should be changed down the cylinder specific maintenance, no blockage and the water output is small indicates that there is scale, the tank water should be changed to dilute hydrochloric acid swishing cycle, clear scale to normal and then change the distilled water. General water in the tank is used to cool the barrel, and the natural water we pass is used to cool the tank. Regularly check the water quality of the cooling water tank, if there is turbidity, should be replaced promptly.
6.Check whether the solenoid valve is working properly, the coil has not burned out if there is a timely replacement.
7. The temperature does not rise to quite the temperature continues to rise and fall may exist for the following reasons: whether the day electric couples loose fall; heater relay is working properly; solenoid valve is working properly, timely replacement of deformation of the heater, and tighten the screws.
8. Timely clean up the dirt in the vacuum tank, and the material in the exhaust chamber so that the pipeline is smooth. Vacuum pump seals need to be replaced promptly if there is wear and tear regular inspection, the output shaft jumping is bearing damage and shaft fracture must be opened and replaced, such as the gearbox two output shaft bearing position wear is too serious, the box must be replaced to avoid greater loss of failure.
9, To drive the screw rotation of the DC motor to focus on checking the brush wear and contact, the insulation resistance value of the motor whether in the specified value should also be measured frequently. In addition, check the connection line and other components that are rusted, and the use of protective measures.
10. When the single-screw extruder needs to stop using for a long time, should be in the screw, Jane, the head, and other working surfaces coated with anti-rust grease. The small screw should be suspended in the air or placed in a special wooden box, and a wooden block pad flat, so as not to deform the screw or bruise.
11. Single-screw extruder attached to the cooling water pipe wall is prone to scale external corrosion and rust. Maintenance should be carefully checked, too much scale will block the pipeline, can not achieve the cooling effect, rust will be serious leaks, so maintenance must take descaling and anti-corrosion cooling measures.
12. Designate a person responsible for the maintenance of equipment. And each maintenance and repair detailed record is included in the plant equipment management files.
If you still have questions, you can consult our company, we are happy to answer for you. The company insists on the purpose of "quality first, customer first", and warmly welcomes new and old customers to cooperate with us.
The composition of the single screw extruder: mainly consists of servo motor, reduction box, screw cylinder, nozzle head, filter air, heating and cooling system, touch screen, and SPS control. It is the extrusion host to form.
What are the reasons why the main engine of the single screw extruder cannot be started and the solutions?
What are the reasons and solutions for the high inlet flow of the single screw extruder?
What is the design concept of the single screw extruder?
1. Reasons:
(1) The driving program of the single screw extruder is wrong.
(2) There is a problem with the main engine thread and whether the fuse is blown.
(3) The locking device for the single screw extruder and the main engine works.
2. Treatment:
(1) Check the program of the insert extruder and restart in the correct order.
(2) Check the main engine circuit.
(3) Check whether the lubricating oil pump has started and check the status of the locking device concerning the main engine. The oil pump cannot be turned on and the engine cannot be turned on.
(4) The inverter has not discharged the induction current, turn off the main power supply and wait five minutes before starting.
(5) Check if the emergency button of the single screw extruder has been reset.
1. Reasons: (1) The single screw extruder has an insufficient heating time and a large torque. (2) A certain section of the heating does not work.
2. Treatment method: (1) Use the handwheel when driving the single screw extruder. If it is not easy, extend the heating time or check that the heaters of the individual sections work properly.
The main engine makes an abnormal noise:
1. Reasons: (1) Main engine stock damaged. (2) A specific SCR in the SCR DC power supply of the main engine is damaged.
2. Treatment method: (1) Replace the main engine stock of the single screw extruder. (2) Check the thyristor alignment and replace the thyristor component if necessary.
1. High-speed and high-Yield extrusion based on high quality.
2. The design concept of low-temperature plasticization ensures the extrusion of high-quality products.
3. The two-stage overall design of the single screw extruder reinforces the plasticization function to ensure the adjustment of the high-performance extrusion.
4. Special barrier, comprehensive mixing design to ensure the mixing effect of materials.
5. High torque drop, extra-large pressure bearing.
6. Gears and shafts are made of high-strength alloy steel, cooled, and chipped.
7. High hardness, high finish, extremely quiet.
8. PLC-intelligent control can realize the connection between main and auxiliary machines.
9. The easy-to-monitor human-machine interface makes it easy to understand the processing and machine status.
10. The control method (temperature device) can be changed if necessary.
11. The material is 38CrMoAL/A nitric treatment, wear-resistant.
12 Strict temperature control accuracy, combined with air cooling and water cooling.
13. The single screw extruder has a unique inlet design and complete water cooling.
14. An single screw extruder with a grooved surface of the lower shell has an improved feed function that guarantees a high speed and a high yield of extrusion.
The single screw extruder is increasingly used in industrial production.Nanjing JlEYA has committed itself to offering the best-suited single screw extruders at a reasonable price, and all that is necessary to meet the needs of the customer.
PVC compounding extruder is made by mixing PVC resin with stabilizers, lubricants, and other additives through granulation and then extrusion, or by using powder in one extrusion. what are the application areas of PVC? The following are the details.
Here is the content list:
General soft products
PVC film
PVC foam products
PVC coated products
PVC paste resin
PVC transparent sheet
PVC rigid sheet
Other applications of PVC
General soft products can be extruded into cables, wires, and hoses by the extruder: shoe soles, slippers, various plastic sandals, as well as toys and auto parts by the injection molding machine with various molds.
PVC film After mixing and plasticizing PVC with additives, transparent or colored film of specified thickness can be made by using a three-roller or four-roller calendar, and calendered film can be processed by this method. It can also be cut and heat laminated to process raincoats, tablecloths, curtains, packaging bags, inflatable toys, etc. The wide transparent film can be used for greenhouse, plastic shed, and ground film; the film stretched in both directions can be used for shrink packaging due to its characteristics of shrinkage by heat.
Soft PVC can be used as sandals, insoles, foam slippers, and shockproof and cushioning packaging materials. In addition, it can also be extruded into low-foaming hard PVC sheets and profiles by extruder, which is a new type of building material and can be used as a substitute for wood.
Artificial leather with backing is made by coating PVC paste on cloth or paper and then plasticizing it at 100 degrees Celsius or above (or PVC and additives can be calendered into film and then pressed together with backing); while artificial leather without backing is directly calendered by calender into soft sheet with a certain thickness and then pressed with the pattern. It can be used to make leather bags, leather boxes, book covers, sofas, and car cushions, etc. It can also be made into flooring leather, which is used as the flooring material for buildings.
PVC emulsion or micro-suspension resin is dispersed in a liquid plasticizer to make it swell and plasticize into the plasticized sol, and then add stabilizer, filler, coloring agent, etc. After full stirring for de-bubbling, PVC paste is prepared, and then processed into various products such as coat hangers, tool handles, Christmas trees, etc. by casting, impregnating, or laminating processes.
Impact modifier and organotin stabilizer are added to PVC, which is mixed, plasticized, and calendered into transparent sheets. Then it can be made into thin-walled transparent containers by thermoforming and can be used for vacuum blister packaging such as moon cake boxes, etc. It is an excellent packaging material and decoration material.
PVC hard sheet and plate After adding stabilizer, lubricant, and filler to PVC and mixing, it can be extruded into various caliber hard pipes, shaped pipes, corrugated pipes, and other products by using an extruder, and used as a downpipe, drinking water pipe, electric wire casing or staircase handrail, etc.; the calendered sheet can be overlapped and hot-pressed to make various thicknesses of hard sheets, which can be cut into various desired shapes and can be welded into various chemical resistant tanks, ducts and containers by using PVC welding rod with hot air, etc.
PVC can be processed into rigid profiles using an extruder and used for window and door assembly. In some countries, the doors and windows assembled by PVC rigid profile have occupied the market of windows and doors together with wooden windows and doors, aluminum windows, etc.
If you want to buy PVC compounding extruder, you can consult our company, our company's website is https://www.njjyextrusion.com/
The twin screw extruder's standard equipment includes a sturdy base frame dedicated to housing the temperature control unit and oil lubrication system. The equipment features advanced control software for seamless integration into digital factories, ready for Industry 4.0, greatly improving ease of use. The following is a detailed description of the operating procedures of the twin screw extruder.
Here is the content list:
l Start up operation
l Stop the machine
l Precautions
Start up operation
1.Close the power main gate of the twin screw extruder.
2. Turn on the power at the operation panel: Press and hold the power button clockwise to turn and then release.
3. Set the temperature of each temperature zone: for example, a zone temperature according to the process requirements set the corresponding temperature, press the set button, and then adjust the up and down arrows to the desired temperature, press the set button.
4. Set the feeding rate: according to the process, requirements can be fed rate between 0 ~ 10 to set.
5. Set the host speed of the twin screw extruder: set the host speed between 0~30 according to the process requirements.
6. Add cooling water to the cooling tank.
7. In turn on the fan: press the operation button on the operation panel.
8. When you need to start the operation of the vacuum pump, you can start the vacuum pump.
9. Turn on the cutter switch.
1. Twin screw extruder normal stopping sequence: stop the feeder: close the vacuum line valve, open the vacuum chamber on the cover; gradually reduce the main screw speed; shut down the pelletizer and other auxiliary equipment: off the motor, each external water inlet valve.
2. Twin screw extruder emergency stop: (1) in case of an emergency need to stop the host, you can quickly press the electrical control cabinet red emergency stop button, and the host and the feed speed knob back to zero, and then the total power switch off. After eliminating the fault, you can restart the machine again in normal driving order. (2) encounter equipment automatic protection trip stop: need to set the various parameters knob to zero, and then reset the parameters, press the reset button and start the machine again.
1. The normal production of the first shift machine, be sure to first check whether the barrel, hopper seal is the original closed kind, such as changes or damage, should check the hopper, the machine inside the Jane there are no foreign objects.
2. Pay attention to the screw to start at a low speed, the air time can not exceed 3min.
3. Must pay attention to check the purity of each batch of material, do not allow any impurities mixed into the material.
4. The beginning of the material to pay attention to the first small amount, evenly added material, while paying attention to observe the current meter (torque meter) pointer changes.
For granular material, use metering to add material. When you first start to feed production, be sure to pay attention to the extruder production work overload phenomenon. After the forming die lip out of the material, and then gradually increase the screw speed as appropriate.
5. Often check the working condition of the motor carbon brush, abnormalities should be replaced or adjusted promptly.
6. The screw cleaning work is not allowed to use steel tools scraping material, the application of copper brush, shovel cleaning.
7. When the process temperature is suspected of displaying problems on the instrument, use mercury temperature, meter actual measurement of the machine Jane, and molding mold degree. Refer to the mercury temperature measured temperature, adjust the calibration instrument to show the temperature.
If you still have questions, you can consult our company. Our company's website is https://www.njjyextrusion.com/