PVC compounding extruder is divided into RPVC pipe and SPVC pipe, RPVC pipe is easy to cut, welding, bonding, heating can be bent and therefore very easy to install and use. SPVC pipe has excellent chemical stability excellent electrical insulation and good flexibility and colorability this pipe is often used to replace rubber pipe to transport liquid and corrosive media also used as cable casing and wire insulation pipe, etc. So how do choose raw materials and the operation of PVC compounding extruder? The following is a detailed introduction
Here is the content list:
Raw material selection
Safety operating procedures
PVC compounding extruder in the production of hard pipe resin should be selected from the lower polymerization degree of SG-5 resin polymerization degree of the higher its physical and mechanical properties and heat resistance is better, but the resin liquidity is poor to bring some difficulties in processing, so generally choose viscosity of 1.7 ~ 1.8 × 10-3Pa-s SG-5 resin is appropriate. Hard pipe generally uses lead-based stabilizers whose thermal stability is good commonly used trisodium lead but its lubricity is poor usually and good lubricity of lead, barium soap type and use. Processing hard tube lubricant selection and use are very important to consider both internal lubrication to reduce intermolecular forces to reduce the viscosity of the melt are conducive to molding and to consider external lubrication to prevent the melt and hot metal adhesion to make the product surface shiny. Internal lubrication is generally used metal soap type external lubrication with low melting point wax. Filler mainly with calcium carbonate and barium barite powder calcium carbonate to make the pipe surface performance of good barium can improve the molding of the pipe easy to shape both can reduce costs but the amount of too much will affect the performance of the pipe pressure pipe and corrosion-resistant pipe is best not to add or add less filler.
1. Personnel without induction test and operation training cannot operate the extruder independently.
2. People who have poor eyesight and slow response can not be on duty to operate.
3. Before starting the machine to do a good job of environmental health around the PVC compounding extruder equipment, equipment around the pile of items not related to production.
4. Check the safety settings of the extruder before production for damage and test whether it can work effectively. Check whether the connection bolts are loose and whether the safety guards are firm.
5. Check the lubrication parts, remove the dirt, and refill the lubricant.
6. PVC compounding extruder barrel and die heating constant temperature time to ensure that the material temperature does not reach the process requirements when driving production.
7. Before starting the screw drive motor to use the hand plate support V pulley, should be flexible rotation, no blocking phenomenon; then start the lubricating oil pump work 3min before starting the screw rotation at low speed.
8. Screw airlift time should not exceed 2 ~ 3min.
9. PVC compounding extruder barrel before adding material to check the barrel, hopper, there is no foreign matter; raw materials should be free of metal, sand, and other impurities to Prevent damage to the screw.
10. The screw starts, the transmission parts work sound normal, the main motor current within the allowable rated value, before allowing the barrel to add material, adding material should first be a small amount of evenly added material.
11. When adjusting the die gap or clearing the dirty material, the operator should wear gloves and not face the barrel and die to prevent the molten material from spraying out of the die and scalding the body.
12. Extruder driving operation is not allowed to repair, and no one is allowed to do any work on the equipment at this time.
13. In case of the following phenomena, should be an emergency stop.
Bearing parts of the high temperature, lubricating oil (grease) out; motor odor, smoke, or shell temperature is too high; speed box lubricating oil temperature, smoke; transmission parts emit irregular abnormal sound; machine work produces violent vibration; screw suddenly stop rotating.
14. PVC compounding extruder equipment on the safety cover and the location of the safety alarm device is not allowed to change at will, not to mention artificially caused by the malfunction.
15. Find that the equipment leakage, oil leakage phenomenon should be timely maintenance troubleshooting, no water, oil flow around the machine.
If you have questions about how to use the PVC composite extruder, you can contact us on the official website. We are happy to answer for you.
In plastic extrusion molding equipment, the plastic extruder is usually called the main machine, while its subsequent equipment plastic extrusion molding machine is called the auxiliary machine. Plastic extruders can produce a variety of plastic products. Therefore, the plastic extrusion molding machine is one of the widely used machines in the plastics processing industry, both now and in the future. So what are the characteristics of plastic extruders? The following is a detailed introduction.
Here is the content list:
Modularity and specialization
High efficiency and multi-functionalization
Enlargement and precision
Intelligent and networked
The modular production of plastic extruders can adapt to the special requirements of different users, shorten the research and development cycle of new products, and strive for a larger market share; while specialized production can arrange the production of each system module component of extrusion molding equipment at a fixed point or even for global procurement, which is very beneficial to ensure the quality of the whole period, reduce costs and accelerate the capital turnover.
The high efficiency of plastic extruders is mainly reflected in the high output, low energy consumption, and low manufacturing cost. In terms of function, the screw plastic extruder has been used not only for extrusion molding and mixing processing of polymer materials but its use has been broadened to food, feed, electrode, explosives, building materials, packaging, pulp, ceramics, and other fields.
Achieving the large-scale plastic extruder can reduce the production cost, which is a more obvious advantage in the large twin-screw plastic pelletizing set, film blowing set, pipe extrusion set, etc. National key construction services required for major technical equipment, large-scale ethylene project supporting one of the three key equipment of large extrusion pelletizing unit long-term dependence on imports, so we must accelerate the localization process to meet the development needs of the petrochemical industry.
Plastic extruders in developed countries have generally used modern electronic and computer control technology, the entire extrusion process parameters such as melt pressure and temperature, the temperature of each section of the body, the main screw and feeding screw speed, feeding volume, the ratio of various raw materials, motor current and voltage and other parameters for online detection, and the use of microcomputer closed-loop control. This is extremely beneficial to ensure the stability of process conditions and improve the precision of products.
If you need to buy a plastic extruder, you can consider our cost-effective products. Nanjing JlEYA is the leading manufacturer extruder manufacturer specializing in a twin-screw extruder, mini twin screw extruder, plastic extruder, and parallel twin-screw extruder in China, which is widely used in compounding, modification, polymerization, devolatilization, reaction, recycling, etc. After 17 years of development, now we have a 20,000 square meters workshop with annual sales of over 300+ sets, export over 60 countries.
JIEYA has the most experienced technical core team, with extensive experience in system integration of the development manufacturing, materials processing, application technology, and other fields.
A single-screw extruder consists of an Archimedes screw rotating in a heated barrel. It is widely used because of its simple structure, easy manufacturing, high processing efficiency, and low price, and is the most technically mature and used type of extruder at present. The following is a detailed introduction to single-screw extruders.
Here is the content list:
The design concept of a single-screw extruder
Single-screw extruder features
Uses of single screw extruder
(1) Single-screw extruders are high-speed, high-output extrusions based on high quality, and the design concept of low-temperature plasticization ensures the extrusion of high-quality products. Two-step overall design to strengthen the plasticizing function and ensure the adjustment of high-performance extrusion.
(2) A special barrier of the single-screw extruder, integrated mixing design to ensure material mixing effect and high torque output, extra-large thrust bearing.
(3) The gears and shafts of a single screw extruder are high-strength alloy steel, carburized, ground teeth treatment, high hardness, high finish, and ultra-low noise. PLC intelligent control, the linkage between main and auxiliary machines is possible.
(4) Single screw extruder easy to monitor human-machine interface, easy to understand the processing and machine status, and the control method (temperature control instrument) can be changed as needed.
(5) The material of the single screw extruder is 38CrMoAL/A nitride treatment, which is wear-resistant. It has a combination of air-cooled and water-cooled cooling for strict temperature precision control, and the unique air inlet design makes it a perfect water-cooling device.
(6)Single screw extruder with grooved surface feeding bottom sleeve of screw barrel has enhanced feeding function, which provides a guarantee for high speed and high output extrusion.
1. Hard gearbox, AC or DC stepless drive speed regulation.
2. New screw structure, melt and mix uniformly to ensure low melt temperature and high output
3. Screw barrel material adopts nitride steel 38CrMoAIA nitride treatment, and the surface alloy treatment has higher hardness.
4. Cast copper, cast aluminum heater, air-cooled and water-cooled according to requirements.
5. Advanced electrical control system of single screw
Pipe extrusion of single-screw extruder: it is suitable for PP-R pipe, PE gas pipe, PEX cross-linked pipe, aluminum-plastic composite pipe, ABS pipe, PVC pipe, HDPE silicon core pipe, and various co-extruded composite pipes.
Sheet and plate extrusion: applicable to PVC, PET, PS, PP, PC, and other profiles and plates extrusion. Extrusion of various other plastics such as silk, rod, etc.
Profile extrusion: adjusting the extruder speed and changing the structure of the extrusion screw can be applied to the production of various plastic profiles such as PVC, polyolefin, etc. Modified pelletizing: It is suitable for blending, modifying, and enhancing pelletizing of various plastics.
Nanjing JlEYA is a leading extruder manufacturer specializing in a twin-screw extruder, micro twin-screw extruder, plastic extruder, and parallel twin-screw extruder, which are widely used in compounding, modification, polymerization, devolatilization, reaction, recycling, and other fields. After 17 years of development for many years, now we have a 20,000 square meters plant, 300+ sets of annual sales, and export to more than 60 countries.
The single screw extruder is a special reduction power device designed for plastic and rubber single screw extruder equipment. The reducer is matched with the motor. The gear parts are made of high-strength alloy steel. The gears are processed by carburizing, quenching, and high-precision gear grinding. The gear accuracy is level 6, and the tooth surface hardness is HRC58-62.
What is the principle of single screw extruder?
What is the current industry development of single screw extruder?
What should I pay attention to when using single screw extruder?
The single screw extruder is generally divided into three sections in effective length. The effective length of the three sections is determined according to the diameter of the screw and the pitch and depth of the screw, which are generally divided into one-third of each; the last thread of the single screw extruder has been called the conveying section. It is required that it cannot be plasticized, but it must be preheated and compressed;
The second section of the single screw extruder is called the compression section. At this time, the volume of the screw groove gradually decreases, and the temperature must reach the degree of plasticization of the material. The compression produced here is from the conveying section three, and here it is compressed to one. Some machines also have Change, the plasticized material enters the third stage;
The third section of the single screw extruder is the metering section, where the material maintains the plasticizing temperature to supply the machine head, which is generally slightly higher than the plasticizing temperature.
In single screw extruder equipment, the plastic extruder is normally referred to as the main machine and the following equipment, the plastic extruder, is referred to as the auxiliary machine. After more than 100 years of development, the plastic extruder has been derived from the original single-screw extruder, a variety of models such as double-screw, multi-screw and even non-screw models have been derived. The plastic extruder (host) can be used with different plastic moulding machines such as tube, foil, holding material, monofilament, flat wire, strapping, extruding network, plate material, profile material, pelleting, cable coating, etc. are used. Suitable for different plastic extrusion production lines for the production of different plastic products. Therefore, plastic extrusion machines are today and in the future one of the most common models in the plastics processing industry.
What should I pay attention to when using single screw extruder?
(1) The material convey way of the single screw extruder mainly relies on friction, which limits its feeding performance. And it is difficult to add the powder, paste, glass fiber and inorganic fillers, so pay attention to the material used.
(2) When the pressure of the single screw extruder head is high, the reverse flow will increase and the productivity will decrease. Therefore, always pay attention to the pressure of the equipment.
(3) The surface renewal effect of the single screw extruder material in the exhaust zone is small, so the exhaust effect is poor.
(4) single screw extruder is not suitable for certain processes, such as polymer coloring, thermosetting powder processing, etc.
The single screw extruder has achieved an irreplaceable position in industrial production. Nanjing JlEYA is committed to providing various bending and rolling machines of high quality for all customers from all over the world.
The screw can be said to be the heart of the injection molding machine. The quality of the screw determines the quality of the product. The plasticizing screw of the engineering plastic twin screw extruder has the functions of conveying, melting, mixing, compression, metering and exhausting. It plays an important role in the quality of plasticization and is a key factor affecting the quality of plasticization.
What is the difference between engineering plastic twin screw extruder and single screw extruder?
What are the characteristics of engineering plastic twin screw extruder?
What are the structural principles of engineering plastic twin screw extruder?
1. Price: single screw extruder has simple structure and low price; Engineering plastic twin screen expander is complex and expensive
2. Plasticizing capacity: single screw extruder is suitable for plasticizing and extruding polymers and granular materials. The shear degradation of polymer is small, but the residence time of material in extruder is long; The engineering plastic twin screw extruder has good mixing and plasticizing ability, and the residence time of materials in the extruder is short, which is suitable for powder processing.
3. In terms of processing capacity and energy consumption: the engineering plastic twin screw extruder has large output, fast extrusion speed and low energy consumption per unit output, while the single screw extruder is poor.
4. Operability: the single screw extruder is easy to operate and the process control is simple; The operation of engineering plastic twin screen expander is relatively complex and the process control requirements are high.
1. engineering plastic twin screw extruder is divided into parallel and conical according to the relative position of the two axes;
2. engineering plastic twin screw extruder is divided into meshing type and non-meshing type according to the two screw meshing procedures;
3. engineering plastic twin screw extruder is divided into the same direction and the opposite direction according to the rotation direction of the two screws, and there are inward and outward points in the opposite direction;
4. engineering plastic twin screw extruder is divided into high speed and low speed according to the screw rotation speed;
5. engineering plastic twin screw extruder is divided into whole and combination according to the structure of screw and barrel.
For the basic mechanism of the engineering plastic twin screw extruder process, in simple terms, a screw rotates in the barrel and pushes the plastic forward. The screw structure is an inclined surface or slope wound on the center layer, the purpose of which is to increase the pressure in order to overcome the greater resistance. As far as the engineering plastic twin screw extruder is concerned, there are three kinds of resistance that need to be overcome during work: one is friction, which includes the friction of solid particles (feeding) against the barrel wall and the first few revolutions of the screw (feeding zone). There are two kinds of mutual friction forces; the second is the adhesion of the melt on the cylinder wall; the third is the internal logistics resistance of the melt when it is pushed forward.
Nanjing JlEYA has focused on the development and production of engineering plastic twin screw extruders for several years. And it commits to provide perfect service for every customer from all over the world.
Twin-screw extruders have barrels with an extension range of 4 and 6D, allowing for precise process design to meet specific customer requirements. All barrels allow for precise temperature control. Cooling is achieved by cooling water injection and high-performance electric heating rods for direct and fast heating. The auxiliary equipment of the twin-screw extruder consists of a straightening device, a preheating device, and a cooling and heating device. The following is a detailed description of the auxiliary equipment.
Here is the content list:
l Straightening device
l Preheating device
l Cooling device
One of the most common types of plastic extrusion rejects is eccentricity, and bending of the wire core in various patterns is one of the most important causes of insulation eccentricity. In sheath extrusion, scratches on the sheath surface are also often caused by the bending of the cable core. Therefore, a variety of extrusion units in the straightening device is essential. The main types of straightening devices are roller type (divided into horizontal and vertical type); pulley type (divided into single pulley and pulley group); stranded pulley type, which plays a variety of roles such as dragging, straightening, and stabilizing tension; pressure pulley type (divided into horizontal and vertical type), etc.
Cable core preheating is necessary for both insulation extrusion and sheath extrusion. For the insulation layer, especially the thin layer of insulation, the existence of pores should not be allowed, the core can be completely removed from the surface of the water, oil, and dirt through high temperature preheating before extrusion. For the sheath extrusion, the main role is to dry the cable core, to prevent the role of moisture (or moisture around the bedding layer) to make the sheath in the possibility of porosity. Preheating can also prevent the plastic from being extruded due to sudden cooling and residual internal pressure. In the process of extruding plastic, preheating can eliminate the cold line into the high-temperature heat, in contact with the plastic at the mouth of the die to form a disparity in temperature, to avoid fluctuations in plastic temperature and lead to fluctuations in extrusion pressure, to stabilize the amount of extrusion and ensure the quality of extrusion. Extrusion unit is used in the electric heating core preheating device, requires sufficient capacity, and ensures rapid temperature rise, so that the core preheating and cable core drying efficiency. The preheating temperature is restricted by the speed of wire release, generally similar to the temperature of the head.
The formed plastic extrusion layer after leaving the head should be immediately cooled and shaped, otherwise, deformation will occur under the action of gravity. The way of cooling usually uses water cooling, and according to the water temperature is different, divided into rapid cooling and slow cooling. Rapid cooling is the direct cooling of cold water, rapid cooling of plastic extrusion layer sizing is beneficial, but for crystalline polymers, due to sudden heat cooling, easy to internal residual stress in the extrusion layer organization, resulting in the use of the process of cracking, general PVC plastic layer using rapid cooling. Slow cooling is to reduce the internal stress of the product, in the cooling water tank placed in sections of different temperatures of water, so that the product gradually cool down and set, PE, PP extrusion on the use of slow cooling, that is, after hot water, warm water, cold water three cooling.
If you are engaged in a twin-screw extruder-related industry, you can consider our cost-effective products.
Each type of product in the plastic extruder line has its operating characteristics, and a detailed understanding of its operating characteristics is necessary to give full play to the effectiveness of the machine. The following is a detailed description of the operating procedures and maintenance methods for plastic extruders.
Here is the content list:
Operation procedures
Maintenance methods
The plastic extruder is one of the machine types, master the extruder operation points, the correct and reasonable use of a plastic extruder. The use of plastic screw extruder includes a series of links such as installation, adjustment, commissioning, operation, maintenance, and repair of the machine, and its use has the commonality of general machines, mainly in the drive motor and reduction and speed change device. However, the working system of the plastic screw extruder, the extrusion system, is unique, and special attention should be paid to its characteristics when using the plastic screw extruder. Extruder manuals generally have clear provisions for the installation, adjustment, and commissioning of the machine, here the main points of the operation, maintenance, and repair of the plastic screw extruder are briefly described as follows: in particular, to correctly grasp the structural characteristics of the screw, heating and cooling management instrumentation characteristics and assembly, the correct extrusion process conditions, the correct operation of the machine.
1.Pastic extruder equipment should be placed in a ventilated position to ensure that the heat of the motor work prolongs its life; the machine should be kept well grounded.
⒉Regularly check the tool screws, the plastic extruder after 1 hour of use, with tools to tighten the moving knife, fixed knife screws, to strengthen the fixed between the blade and the knife frame; should be regularly filled with lubricating oil to ensure the lubrication between the bearings; to ensure the sharpness of the cutting edge of the tool, should always check the tool to ensure its sharpness, to reduce unnecessary damage to other parts caused by the blunt lack of the blade; regularly check whether the belt is loose, and timely tightening.
3. Restart - Before starting the plastic extruder for the second time, the remaining debris in the machine chamber should be cleared to reduce the starting resistance. Periodically open the inertia cover and pulley cover to clear the ash outlet under the flange, which can cause the powder to enter the shaft bearing.
4. Replacement parts - When replacing knives, the clearance between the moving and fixed knives should be 0.8 MM for crushers over 20 HP and 0.5 MM for crushers under 20 HP. The thinner the recycled material is, the gap can be adjusted appropriately larger.
If you need to know more, you can consult our company. The company focused on co-rotating twin-screw compounding extruders with the core of the various R&D and manufacturing, such as a twin-screw extruder, mini twin screw extruder, plastic extruder, parallel twin-screw extruder, and so on, the application covers compounding mixing modified granulation, polymerization, devolatilization, step molding, renewable recycling, and other fields.